SABIC Innovative Plastics Xylex HX7409HP PC+POLYESTER (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polyester, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xylex |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xylex HX7409HP PC+POLYESTER (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Low flow, polycarbonate/Polyester alloy; contains mold release. For medical devices and pharmaceutical applications. Healthcare management of change (MoC), biocompatible (ISO 10993 or USP Class VI), food contact compliant. EtO and gamma sterilizable.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.070 % | 0.070 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.28 % @Temperature 23.0 °C |
0.28 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 265 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D 1238 |
| 15 g/10 min @Load 10.0 kg, Temperature 265 °C |
15 g/10 min @Load 22.0 lb, Temperature 509 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D 638 |
| 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
| 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Break | 110 % | 110 % | Type I, 50 mm/min; ASTM D 638 |
| 135 % | 135 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D 638 |
| 6.0 % | 6.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.30 GPa | 334 ksi | 50 mm/min; ASTM D 638 |
| 2.40 GPa | 348 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | 2 mm/min; ISO 178 |
| 95.0 MPa | 13800 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 2.18 GPa | 316 ksi | 2 mm/min; ISO 178 |
| 2.28 GPa | 331 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.800 J/cm @Temperature -30.0 °C |
1.50 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 10.0 J/cm @Temperature 23.0 °C |
18.7 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| 78.0 kJ/m² @Temperature 23.0 °C |
37.1 ft-lb/in² @Temperature 73.4 °F |
63.5*12.7*3.2; ISO 180/4A | |
| Charpy Impact, Notched | 2.20 J/cm² @Temperature 23.0 °C |
10.5 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Impact Test | 85.0 J @Temperature 23.0 °C |
62.7 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature -40.0 - 95.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 95.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 111 °C | 232 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 111 °C @Thickness 3.20 mm |
232 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 127 °C | 261 °F | Rate B/50; ISO 306 |
| 129 °C | 264 °F | Rate B/120; ISO 306 | |
| 130 °C | 266 °F | Rate B/50; ASTM D 1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 79 % @Thickness 2.54 mm |
79 % @Thickness 0.100 in |
ASTM D 1003 |
Users viewing this material also viewed the following:
- PolyOne LubriOne™ PS-30GF/15T Natural Polybutylene Terephthalate (PBT)
- PolyOne OnFlex™ S EH 50A-3S7002 Thermoplastic Elastomer (TPE)
- Resin Technology Group Fusion 830 General Purpose Fusion Cyanoacrylate
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 60 PHR N774 (SRF) Filler
- Kazanorgsintez Oleox-5
- Solvay Specialty Polymers Polymist® XPP 541 Polytetrafluoroethylene (PTFE)
- Techmer ES HiFill® HDPE GF15 50100 15% Glass Filled
- SABIC Innovative Plastics LNP THERMOCOMP KF008 Acetal Copolymer (Europe-Africa-Middle East)
- Aclo Accutech Polypropylene Homopolymer HP0339M40L Mica Reinforced
- CENTROPLAST CENTRODAL GL Polyoxymethylene + PE-UHMW
Copyright © lookpolymers.com All Rights Reserved