SABIC Innovative Plastics Xylex FXY391DF PC+POLYESTER (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xylex
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Xylex FXY391DF PC+POLYESTER (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC+Polyester alloy in Diffusion Visual fx. This grade is compliant with US FDA/European food contact regulations. Color package may influence performance.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D 792
Density 1.17 g/cc
0.0423 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.010 %
0.010 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.010 %

@Temperature 23.0 °C
 0.010 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 10 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 10 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
11 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 11 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa
8700 psi
50 mm/min; ISO 527
63.0 MPa
9140 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 61.0 MPa
8850 psi
Type I, 50 mm/min; ASTM D 638
61.0 MPa
8850 psi
50 mm/min; ISO 527
Elongation at Break 110 %
110 %
Type I, 50 mm/min; ASTM D 638
125 %
125 %
50 mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
Type I, 50 mm/min; ASTM D 638
6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 2.13 GPa
309 ksi
50 mm/min; ASTM D 638
2.30 GPa
334 ksi
1 mm/min; ISO 527
Flexural Strength 89.0 MPa
12900 psi
2 mm/min; ISO 178
Flexural Yield Strength 86.0 MPa
12500 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.15 GPa
312 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.21 GPa
321 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.810 J/cm

@Temperature -30.0 °C
 1.52 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
0.880 J/cm

@Temperature 23.0 °C
 1.65 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
7.00 kJ/m²

@Temperature 23.0 °C
 3.33 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 0.600 J/cm²

@Temperature 23.0 °C
 2.86 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 67.0 J

@Temperature 23.0 °C
 49.4 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 69.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 38.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
71.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 39.4 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 38.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
72.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 40.0 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 118 °C

@Thickness 3.20 mm
 244 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 113 °C
235 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
105 °C

@Thickness 3.20 mm
 221 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 122 °C
252 °F
Rate B/50; ISO 306
123 °C
253 °F
Rate B/50; ASTM D 1525
124 °C
255 °F
Rate B/120; ISO 306