SABIC Innovative Plastics LNP LUBRICOMP DBP32EI PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DBP32EI PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* DBP32EI is a compound based on Polycarbonate resin containing 15% PTFE/Silicone and 10% Glass Bead. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ASTM D792 |
| 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0058 cm/cm @Time 86400 sec |
0.0058 in/in @Time 24.0 hour |
ISO 294 |
| 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0071 cm/cm @Time 86400 sec |
0.0071 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ASTM D638 |
| Tensile Strength, Yield | 15.0 MPa | 2180 psi | ASTM D638 |
| Elongation at Break | 8.8 % | 8.8 % | ASTM D638 |
| Tensile Modulus | 4.13 GPa | 599 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 64.0 MPa | 9280 psi | ISO 178 |
| 68.0 MPa | 9860 psi | ASTM D790 | |
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
| 2.75 GPa | 399 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.33 J/cm | 2.49 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.45 J/cm | 17.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 68.0 kJ/m² | 32.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.51 | 0.51 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.53 | 0.53 | ASTM D3702 Modified |
| K (wear) Factor | 238 x 10-8 mm³/N-M | 118 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 121 °C @Thickness 3.20 mm |
250 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® CFR9111 PC COPOLYMER (Asia Pacific)
- ICE Al2O3 94
- SABIC Innovative Plastics ULTEM CRS5011 PEI
- Solvay TOLCIDE® PS 70A 70% tetrakis hydroxymethyl phosphonium sulfate
- SABIC Innovative Plastics Valox® SLWM2105 PBT+PC (Asia Pacific)
- Teknor Apex TruVis Esters™ TNTM TriNonyl Trimellitate
- Borealis CA7230 Low Density Polyethylene
- Dow Corning LSPOG50 SILICONE MASTERBATCH ORANGE
- ExxonMobil LD 307.76 Clear, High Impact Film Resin
- Arlon LW401A##-P3 0.040" (1.02 mm) Cured Self-Fusing Silicone Tape (Triangular, Unsupported)
Copyright © lookpolymers.com All Rights Reserved