SABIC Innovative Plastics Xenoy® X5100 PC+PBT (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xenoy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Xenoy® X5100 PC+PBT (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
XENOY X5100 is a semi-crystalline, impact modified PC-PBT blend with excellent flow. (PC+PBT-I).
Physical Properties Metric English Comments
Density 1.22 g/cc
0.0441 lb/in³
ISO 1183
Moisture Absorption 0.150 %
0.150 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.50 %
0.50 %
ISO 62
Viscosity 215000 cP
215000 cP
Melt Viscosity, 260°C, 1500 sec-1; ISO 11443
Linear Mold Shrinkage, Flow 0.0070 - 0.010 cm/cm
0.0070 - 0.010 in/in
on Tensile Bar; SABIC Method
Melt Index of Compound 13 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 13 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
50 mm/min; ISO 527
Tensile Strength, Yield 54.0 MPa
7830 psi
50 mm/min; ISO 527
Elongation at Break 50 %
50 %
50 mm/min; ISO 527
Elongation at Yield 4.5 %
4.5 %
50 mm/min; ISO 527
Tensile Modulus 2.15 GPa
312 ksi
1 mm/min; ISO 527
Flexural Yield Strength 80.0 MPa
11600 psi
2 mm/min; ISO 178
Flexural Modulus 2.05 GPa
297 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 45.0 kJ/m²
21.4 ft-lb/in²
80*10*4; ISO 180/1A
18.0 kJ/m²

@Temperature -30.0 °C
 8.57 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
20.0 kJ/m²

@Temperature -20.0 °C
 9.52 ft-lb/in²

@Temperature -4.00 °F
 80*10*4; ISO 180/1A
35.0 kJ/m²

@Temperature -10.0 °C
 16.7 ft-lb/in²

@Temperature 14.0 °F
 80*10*4; ISO 180/1A
40.0 kJ/m²

@Temperature 0.000 °C
 19.0 ft-lb/in²

@Temperature 32.0 °F
 80*10*4; ISO 180/1A
Charpy Impact Unnotched NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 5.00 J/cm²
23.8 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
1.50 J/cm²

@Temperature -30.0 °C
 7.14 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eA
4.00 J/cm²

@Temperature 0.000 °C
 19.0 ft-lb/in²

@Temperature 32.0 °F
 Edgew 80*10*3 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 85.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 47.2 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 44.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 105 °C
221 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 84.0 °C
183 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 117 °C
243 °F
Rate B/50; ISO 306
120 °C
248 °F
Rate B/120; ISO 306
135 °C
275 °F
Rate A/50; ISO 306
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C PASSES
IEC 60695-10-2