SABIC Innovative Plastics Xenoy® X4810 PBT+PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® X4810 PBT+PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Xenoy X4810 is a hydrostable, High Modulus Ductile PC/PBT blend. This resin provides low temperature (below 0C) ductile impact behaviour, high chemical resistance, very low creep, low CTE, excellent fatique and high heat dimensional stability. Xenoy X4810 resin can be considered for body panels, safety equipment, housings, doorhandles, spring-loaded applications, medical device enclosures, outdoor sports equipment.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.140 % | 0.140 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.42 % | 0.42 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0070 - 0.0090 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 12 g/10 min @Load 5.00 kg, Temperature 266 °C |
12 g/10 min @Load 11.0 lb, Temperature 511 °F |
ASTM D1238 |
| Melt Index of Compound | 10 g/10 min @Load 5.00 kg, Temperature 265 °C |
10 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 105 MPa | 15200 psi | ISO 2039-1 |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D638 | |
| 65.0 MPa | 9430 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | Type I, 5 mm/min; ASTM D638 |
| 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 | |
| 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D638 | |
| 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 100 % | 100 % | 5 mm/min; ISO 527 |
| 100 % | 100 % | 50 mm/min; ISO 527 | |
| 150 % | 150 % | Type I, 50 mm/min; ASTM D638 | |
| 150 % | 150 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 4.1 % | 4.1 % | 5 mm/min; ISO 527 |
| 4.1 % | 4.1 % | 50 mm/min; ISO 527 | |
| 4.5 % | 4.5 % | Type I, 50 mm/min; ASTM D638 | |
| 4.7 % | 4.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.75 GPa | 399 ksi | 1 mm/min; ISO 527 |
| 2.90 GPa | 421 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 87.0 MPa | 12600 psi | 2 mm/min; ISO 178 |
| 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 |
| 2.70 GPa | 392 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 7.50 J/cm | 14.1 ft-lb/in | ASTM D256 |
| 1.50 J/cm @Temperature -30.0 °C |
2.81 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| 5.00 J/cm @Temperature 0.000 °C |
9.37 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80*10*4; ISO 180/1A |
| 12.0 kJ/m² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| 20.0 kJ/m² @Temperature 0.000 °C |
9.52 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 5.00 J/cm² | 23.8 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 70.0 J @Temperature 23.0 °C |
51.6 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| 70.0 J @Temperature -20.0 °C |
51.6 ft-lb @Temperature -4.00 °F |
ASTM D3763 | |
| Impact Test | 110 J | 81.1 ft-lb | Multiaxial Impact; ISO 6603 |
| Taber Abrasion, mg/1000 Cycles | 30 | 30 | CS-17, 1 kg; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 69.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 80.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
44.4 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 83.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 90.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
50.0 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 | |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 120 °C @Thickness 3.20 mm |
248 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 98.0 °C @Thickness 3.20 mm |
208 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 131 °C | 268 °F | Rate B/50; ASTM D1525 |
| 131 °C | 268 °F | Rate B/50; ISO 306 | |
| 133 °C | 271 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP FARADEX NX07344 PC+ABS (Asia Pacific)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Hercoflex 600 Plasticizer
- Eastman Eastar MN059 Copolyester
- DuPont Performance Polymers Crastin® LW9020FR BK851 PBT+ASA (Unverified Data**)
- Aclo Accutech Polypropylene Homopolymer HP0334C40L1 Calcium Reinforced
- 3M K37 Glass Bubbles
- 3M Scotchkote™ 413/215 Patch Compound
- 3M Scotch-Weld™ RT41 Retaining Compound Anaerobic Adhesives
- Voloknohim PA-TM15 Glass and Mineral Filled
- ChevronTexaco URSA® SAE 10W-30 Premium TDX
Copyright © lookpolymers.com All Rights Reserved