SABIC Innovative Plastics Xenoy® EXXY0113 PBT (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xenoy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Xenoy® EXXY0113 PBT (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Blow Moldable Impact modified XENOYThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc
1.22 g/cc
ASTM D 792
Density 1.22 g/cc
0.0441 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.010 %
0.010 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.10 %

@Temperature 23.0 °C
 0.10 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0285 - 0.0335 cm/cm

@Thickness 3.20 mm
 0.0285 - 0.0335 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 4.0 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 4.0 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 ASTM D 1238
9.0 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 9.0 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 38.0 MPa
5510 psi
50 mm/min; ISO 527
48.0 MPa
6960 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 31.0 MPa
4500 psi
50 mm/min; ISO 527
35.0 MPa
5080 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 167 %
167 %
50 mm/min; ISO 527
238 %
238 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 11 %
11 %
Type I, 50 mm/min; ASTM D 638
14.4 %
14.4 %
50 mm/min; ISO 527
Tensile Modulus 1.69 GPa
245 ksi
5 mm/min; ASTM D 638
1.70 GPa
247 ksi
1 mm/min; ISO 527
Flexural Yield Strength 48.0 MPa
6960 psi
2 mm/min; ISO 178
51.0 MPa
7400 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 1.42 GPa
206 ksi
2 mm/min; ISO 178
1.65 GPa
239 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 1.86 J/cm

@Temperature -30.0 °C
 3.48 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
8.02 J/cm

@Temperature 23.0 °C
 15.0 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Notched (ISO) 22.0 kJ/m²

@Temperature -30.0 °C
 10.5 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
95.0 kJ/m²

@Temperature 23.0 °C
 45.2 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 12.9 J/cm²

@Temperature 23.0 °C
 61.4 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 54.0 J

@Temperature 23.0 °C
 39.8 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 83.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 46.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
83.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 46.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 170 µm/m-°C

@Temperature -40.0 - 40.0 °C
 94.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
170 µm/m-°C

@Temperature -40.0 - 40.0 °C
 94.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 46.0 °C
115 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
47.0 °C

@Thickness 3.20 mm
 117 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 115 °C
239 °F
Rate B/50; ASTM D 1525
115 °C
239 °F
Rate B/120; ISO 306
118 °C
244 °F
Rate B/50; ISO 306