LyondellBasell Hifaxâ„¢ ETA3081HS Thermoplastic Polyolefin Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin |
| Manufacturer | LyondellBasell |
| Trade Name | Hifax™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hifaxâ„¢ ETA3081HS Thermoplastic Polyolefin Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hifaxâ„¢ ETA3081HS medium melt flow, 800 MPa flexural modulus, paintable thermoplastic elastomeric olefin (TEO) resin has balanced physical properties, moldability and paintability. Like its lower shrinkage counterpart, ETA3081, ETA3081HS was designed for a wide variety of painted and molded-in color automotive exterior components. Uses: Automotive applicationsInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ISO 1183 |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
7.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 61 | 61 | ISO 868 |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ISO 527-1, -2 |
| Tensile Strength, Yield | 16.0 MPa | 2320 psi | ISO 527-1, -2 |
| Elongation at Break | 500 % | 500 % | ISO 527-1, -2 |
| Elongation at Yield | 15 % | 15 % | ISO 527-1, -2 |
| Flexural Modulus | 0.800 GPa | 116 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.80 kJ/m² @Temperature -40.0 °C |
4.19 ft-lb/in² @Temperature -40.0 °F |
ISO 180 |
| 50.0 kJ/m² @Temperature 10.0 °C |
23.8 ft-lb/in² @Temperature 50.0 °F |
ISO 180 | |
| 54.0 kJ/m² @Temperature 23.0 °C |
25.7 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Gardner Impact | 34.0 J @Temperature -30.0 °C |
25.1 ft-lb @Temperature -22.0 °F |
ASTM D3029, tested in accordance with ASTM D5420 |
| Dart Drop, Total Energy | 23.0 J @Temperature -30.0 °C |
17.0 ft-lb @Temperature -22.0 °F |
Instrumented Energy at Maximum Load, Ductile Failure; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 63.9 °C | 147 °F | Unannealed; ISO 75B-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 43.9 °C | 111 °F | Unannealed; ISO 75A-1, -2 |
| Shrinkage | 1.2 % | 1.2 % | Tool, 100x150x3.2 mm; Basell Test Method |
| 1.60 % @Temperature 121 °C, Time 3600 sec |
1.60 % @Temperature 250 °F, Time 1.00 hour |
Afterbake, 100x150x3.2 mm; Basell Method |
Users viewing this material also viewed the following:
- Niagara LaSalle 4140 Cold Finished Steel Bar
- Samsung Cheil Industries Starex® PT-0180 ABS, Unreinforced Painting Grade
- Teknor Apex Monprene® MP 1061 Thermoplastic Elastomer
- Techmer ES Electrablend® PA6 04001 BK MB Glass/Stainless Steel Filled
- Covestro Makrolon® 6385 Polycarbonate, Injection Grade
- EMS-Grivory Grivory® XE 5026 (BG-30 H) PA6-GF30
- DuPont Performance Polymers Zytel® RS LC3030 NC010 Nylon 610 (Unverified Data**)
- Dow Corning 1248 Fluid
- Arlon Thermabond® 99730N004 0.004" (0.102 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
- LATI Latishield 52/5-07A PP Homopolymer, Steel Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved