SABIC Innovative Plastics ValoxÂ® SHF436HR PBT (Asia Pacific)

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Valox®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics ValoxÂ® SHF436HR PBT (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PBT, Super High Flow, 30% glass reinforced,hydrolytically resistant.

Physical Properties	Metric	English	Comments
Specific Gravity	1.53 g/cc	1.53 g/cc	ASTM D792
Density	1.53 g/cc	0.0553 lb/inÂ³	ISO 1183
Moisture Absorption	0.0600 %	0.0600 %	23Â°C / 50% RH; ISO 62
Water Absorption at Saturation	0.28 %	0.28 %	ISO 62
Linear Mold Shrinkage, Flow	0.0030 - 0.0050 cm/cm @Thickness 3.20 mm	0.0030 - 0.0050 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	30 g/10 min @Load 2.16 kg, Temperature 250 Â°C	30 g/10 min @Load 4.76 lb, Temperature 482 Â°F	ASTM D1238
Melt Index of Compound	30 g/10 min @Load 2.16 kg, Temperature 250 Â°C	30 g/10 min @Load 4.76 lb, Temperature 482 Â°F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	111 MPa	16100 psi	Type I, 5 mm/min; ASTM D638
	117 MPa	17000 psi	5 mm/min; ISO 527
Tensile Strength, Yield	111 MPa	16100 psi	Type I, 5 mm/min; ASTM D638
	117 MPa	17000 psi	5 mm/min; ISO 527
Elongation at Break	2.0 %	2.0 %	Type I, 5 mm/min; ASTM D638
	2.0 %	2.0 %	5 mm/min; ISO 527
Elongation at Yield	2.0 %	2.0 %	Type I, 5 mm/min; ASTM D638
	2.0 %	2.0 %	5 mm/min; ISO 527
Tensile Modulus	9.49 GPa	1380 ksi	1 mm/min; ISO 527
	11.9 GPa	1730 ksi	5 mm/min; ASTM D638
Flexural Yield Strength	163 MPa	23600 psi	1.3 mm/min, 50 mm span; ASTM D790
	165 MPa	23900 psi	2 mm/min; ISO 178
Flexural Modulus	7.72 GPa	1120 ksi	2 mm/min; ISO 178
	8.70 GPa	1260 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	0.920 J/cm	1.72 ft-lb/in	ASTM D256
	0.950 J/cm @Temperature -30.0 Â°C	1.78 ft-lb/in @Temperature -22.0 Â°F	ASTM D256
Izod Impact, Notched (ISO)	8.00 kJ/mÂ²	3.81 ft-lb/inÂ²	80104; ISO 180/1A
	8.00 kJ/mÂ² @Temperature -30.0 Â°C	3.81 ft-lb/inÂ² @Temperature -22.0 Â°F	80104; ISO 180/1A
Charpy Impact, Notched	0.800 J/cmÂ²	3.81 ft-lb/inÂ²	Edgew 80104 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy	6.00 J @Temperature 23.0 Â°C	4.43 ft-lb @Temperature 73.4 Â°F	ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	100 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	55.6 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	100 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	55.6 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	30.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	16.7 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	30.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	16.7 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi)	206 Â°C	403 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	214 Â°C @Thickness 3.20 mm	417 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Vicat Softening Point	200 Â°C	392 Â°F	Rate B/50; ASTM D1525
	200 Â°C	392 Â°F	Rate B/50; ISO 306
	200 Â°C	392 Â°F	Rate B/120; ISO 306