SABIC Innovative Plastics Valox® ENH8560 PBT+PET (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® ENH8560 PBT+PET (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Non-Brominated & Non-Chlorinated Flame Retardant, 30% Glass fiber reinforced PBT/PET blend
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.58 g/cc | 1.58 g/cc | ASTM D792 |
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 |
| Filler Content | 30 % | 30 % | ASTM D229 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.30 % | 0.30 % | ISO 62 |
| Viscosity | 155000 cP | 155000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in | on Tensile Bar; SABIC Method |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 265 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
| 11 g/10 min @Load 5.00 kg, Temperature 250 °C |
11 g/10 min @Load 11.0 lb, Temperature 482 °F |
ISO 1133 | |
| 11 g/10 min @Load 5.00 kg, Temperature 250 °C |
11 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 | |
| Melt Index of Compound | 10 g/10 min @Load 5.00 kg, Temperature 250 °C |
10 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ASTM D1238 |
| 25 g/10 min @Load 5.00 kg, Temperature 265 °C |
25 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ISO 2039-2 |
| Hardness, H358/30 | 166 MPa | 24100 psi | ISO 2039-1 |
| Tensile Strength at Break | 103 MPa | 14900 psi | Type I, 5 mm/min; ASTM D638 |
| 105 MPa | 15200 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 103 MPa | 14900 psi | Type I, 5 mm/min; ASTM D638 |
| 105 MPa | 15200 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| 2.0 % | 2.0 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Elongation at Yield | 1.0 % | 1.0 % | Type I, 5 mm/min; ASTM D638 |
| 1.0 % | 1.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 12.0 GPa | 1740 ksi | 5 mm/min; ASTM D638 |
| 12.0 GPa | 1740 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 145 MPa | 21000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 165 MPa | 23900 psi | 2 mm/min; ISO 178 | |
| Flexural Yield Strength | 145 MPa | 21000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 165 MPa | 23900 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 10.0 GPa | 1450 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 10.0 GPa | 1450 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256 |
| 0.600 J/cm @Temperature 0.000 °C |
1.12 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| 0.600 J/cm @Temperature -30.0 °C |
1.12 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 4.50 J/cm | 8.43 ft-lb/in | ASTM D4812 |
| 4.00 J/cm @Temperature -30.0 °C |
7.49 ft-lb/in @Temperature -22.0 °F |
ASTM D4812 | |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| 7.00 kJ/m² @Temperature 0.000 °C |
3.33 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| 27.0 kJ/m² @Temperature -30.0 °C |
12.8 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179/2C |
| 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179/2C | |
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
10.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 21.0 µm/m-°C @Temperature 23.0 - 150 °C |
11.7 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 56.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
31.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 140 µm/m-°C @Temperature 23.0 - 150 °C |
77.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 210 °C @Thickness 3.20 mm |
410 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Dielectric Strength | 8.00 kV/mm @Thickness 3.20 mm |
203 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| 8.00 kV/mm @Thickness 3.20 mm |
203 kV/in @Thickness 0.126 in |
in oil; ASTM D149 | |
| 25.0 kV/mm @Thickness 1.60 mm |
635 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| 25.0 kV/mm @Thickness 1.60 mm |
635 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 | |
| 35.0 kV/mm @Thickness 0.800 mm |
889 kV/in @Thickness 0.0315 in |
in oil; ASTM D149 | |
| 35.0 kV/mm @Thickness 0.800 mm |
889 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |
| Dissipation Factor | 0.012 @Frequency 1.00e+6 Hz |
0.012 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 0.012 @Frequency 1.00e+6 Hz |
0.012 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | UL 746A |
| 425 V | 425 V | IEC 60112 | |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
Users viewing this material also viewed the following:
- Polymax® Maxelast® A9740 TPE, ABS/PC Overmold
- Grupo Repol Dinalon® B1S25 B30 PA6 30% Glass Beads
- Lucite International Elvacite ® 2927 Acrylic Resin
- A. Schulman POLYBATCH™ Weathered Wood 10418U Concentrate Based In LLDPE
- Vyncolit 2530 W Novolac Phenolic
- 3M AC-251 Black Class B-1/2 Aerospace Sealant
- Arlon 940-07Rxx-P1 0.040" (1.02 mm) Self-Fusing Silicone Tape
- Latrobe Lescalloy® HY-TUF VAC-ARC High Strength Alloy Steel
Copyright © lookpolymers.com All Rights Reserved