Amity Thermosets ATS 132 Phenolic Molding Organic, inorganic, and graphite Filler, Compression Molded

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic
Manufacturer	Amity Thermosets
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Amity Thermosets ATS 132 Phenolic Molding Organic, inorganic, and graphite Filler, Compression Molded.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Characteristics:Self lubricating ( graphite modified )Good glide propertiesGood sealing propertiesMedium or low mechanical strengthUnsuitable for electrical applicationGlossy surfaceThermal conductivityColor-gray Medium flow Applications:SealsSelf lubricating parts / housings , etc. Information provided by Amity Thermosets Limited

Physical Properties	Metric	English	Comments
Density	1.55 - 1.68 g/cc	0.0560 - 0.0607 lb/in³	Molding; IS 867-1963
Apparent Bulk Density	0.740 - 0.840 g/cc	0.0267 - 0.0303 lb/in³	IS 867-1963
Water Absorption	0.20 - 0.30 %	0.20 - 0.30 %	IS 13411-1993
Linear Mold Shrinkage	0.0024 - 0.0036 cm/cm	0.0024 - 0.0036 in/in	IS 13411-1992

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	28.0 - 35.0 MPa	4060 - 5080 psi	5 mm/min.; IS 867-1963
Shear Strength	32.0 - 45.0 MPa	4640 - 6530 psi	IS 867-1963
Izod Impact, Notched	0.170 - 0.270 J/cm	0.318 - 0.506 ft-lb/in	IS 13411-1992

Processing Properties	Metric	English	Comments
Mold Temperature	160 - 180 °C	320 - 356 °F
Injection Pressure	14.7 - 29.4 MPa	2130 - 4260 psi	Mold Pressure
Cure Time	0.550 - 0.750 min	0.00917 - 0.0125 hour	per mm
Shelf Life	12.0 Month	12.0 Month	10-25°C