3M Scotch-Weld™ TE015 Polyurethane Reactive Adhesive

Category	Polymer , Adhesive
Manufacturer	3M
Trade Name	Scotch-Weld™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Scotch-Weld™ TE015 Polyurethane Reactive Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as wood, fiber reinforced plastic (FRP) and many other plastics to themselves, to metal and glass. Extrudable, low viscosity adhesive has a fast set time ideal for bonding wood. Yields thin glue lines.Information provided by 3M

Physical Properties	Metric	English	Comments
Density	1.07 g/cc	0.0387 lb/in³
Brookfield Viscosity	7000 cP	7000 cP	Thermosel using spindle #27

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	65	65
Tensile Strength at Break	27.2 MPa	3950 psi	ASTM D638 Die C
Elongation at Break	750 %	750 %	ASTM D638 Die C
Tensile Modulus	0.172 GPa	25.0 ksi	ASMT D638 Die C
Shear Strength	2.55 MPa @Temperature 23.0 °C	370 psi @Temperature 73.4 °F	Overlap, Polystyrene
	3.41 MPa @Temperature 82.0 °C	495 psi @Temperature 180 °F	Overlap, FRP
	3.79 MPa @Temperature 82.0 °C	550 psi @Temperature 180 °F	Overlap, Maple
	6.52 MPa @Temperature 23.0 °C	945 psi @Temperature 73.4 °F	Overlap, ABS, Substrate Failure
	7.93 MPa @Temperature 23.0 °C	1150 psi @Temperature 73.4 °F	Overlap, Polyacrylic, Substrate Failure
	7.93 MPa @Temperature 23.0 °C	1150 psi @Temperature 73.4 °F	Overlap, PVC, Substrate Failure
	8.791 MPa @Temperature 23.0 °C	1275 psi @Temperature 73.4 °F	Overlap, FRP, Substrate Failure
	11.4 MPa @Temperature 23.0 °C	1650 psi @Temperature 73.4 °F	Overlap, Maple
	12.1 MPa @Temperature 23.0 °C	1760 psi @Temperature 73.4 °F	Overlap, Polycarbonate
Peel Strength	2.10 kN/m	12.0 pli	T-Peel, Initial
	3.68 kN/m	21.0 pli	180°, Polyacrylic
	4.91 kN/m	28.0 pli	180°, FRP
	5.26 kN/m	30.0 pli	T-Peel, Aged 71°C for 2 weeks
	16.3 kN/m	93.0 pli	180°, ABS, Cotton duck failed during testing
	17.5 kN/m	100 pli	180°, Polycarbonate, Cotton duck failed during testing
	17.5 kN/m	100 pli	180°, PVC, Cotton duck failed during testing

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	121 °C	250 °F

Processing Properties	Metric	English	Comments
Cure Time	0.250 min	0.00417 hour	Set Time

Descriptive Properties	Value	Comments
Appearance	White/Off-White