Samsung Cheil Industries Infino® HT-8200G MPPE/PA, Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® HT-8200G MPPE/PA, Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 20 g/10 min @Load 5.00 kg, Temperature 285 °C |
20 g/10 min @Load 11.0 lb, Temperature 545 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength, Yield | 118 MPa | 17100 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 235 MPa | 34100 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 5.88 GPa | 853 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.883 J/cm @Thickness 3.17 mm |
1.65 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 79.0 °C @Thickness 6.40 mm |
174 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 248 °C | 478 °F | B/50; ISO R306 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 9002-SR BLK
- LATI Latilub 73/13-01M POM, Molybdenum disulphide Filled
- SABIC Innovative Plastics Ultem LTX300A PEI Copolymer (Europe-Africa-Middle East)
- Struktol STRUKSILON 8005 Silicone Stabilizer for PU-Rigid Foam
- Eurostar Staramide PF003IX1 PA6, Glass Fiber Filled, Impact Modified, Injection Molded
- Arkema Group OREVAC® 18722 Maleic Anhydride Modified Polypropylene
- Bhansali Engineering Santron IMS 2000 Glitter SAN Resin
- A. Schulman FORMION™ FI 231 5% Mineral Reinforced Ionomer / Nylon Alloy
- Polyplastics Duracon® KT-20 Acetal Co-polymer (POM), Mineral filling, Mineral filling, High rigidity, Wear resistance
Copyright © lookpolymers.com All Rights Reserved