SABIC Innovative Plastics Valox® 350U PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 350U PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Impact modified, UV stabilised, flame retardant polyester with an internal glowwire rating of 850C on 1.6mm flat plaques.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D 792 |
| Water Absorption | 0.14 % @Time 86400 sec |
0.14 % @Time 24.0 hour |
ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.010 - 0.014 cm/cm @Thickness 3.20 mm |
0.010 - 0.014 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 16 g/10 min @Load 5.00 kg, Temperature 250 °C |
16 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 100 % | 100 % | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D 638 |
| Tensile Modulus | 2.25 GPa | 326 ksi | 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.25 GPa | 326 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 7.58 J/cm @Temperature 23.0 °C |
14.2 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 198 µm/m-°C @Temperature -40.0 - 60.0 °C |
110 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C @Thickness 3.20 mm |
180 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Vicat Softening Point | 130 °C | 266 °F | Rate B/50; ASTM D 1525 |
| UL RTI, Electrical | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | UL 746B |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D 257 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D 257 |
| Comparative Tracking Index | 225 V | 225 V | IEC 60112 |
Users viewing this material also viewed the following:
- NHEP Spectron™ E6046 Nylon 6, 15% Glass Fiber
- DuPont Performance Polymers Zytel® FG133F1 NC010 Nylon 66 (Unverified Data**)
- LyondellBasell Hostacomâ„¢ TKS708D Thermoplastic Polyolefin Elastomer
- Teknor Apex Telcar® TL-83-F912-E-UV Thermoplastic Elastomer
- Polyplastics Duranex® 7400F Polybutylene Terephthalate (PBT), Low friction, Low wear, 30% GF filled
- DuPont™ Bynel® 41E871 Anhydride Modified LLDPE
- ChevronTexaco Delo® 100 Motor Oil, SAE 30
- Eastman D4041-P Polyethylene (discontinued **)
- PSM Industries PM Krupp 17-4PH Stainless Steel
- SABIC Innovative Plastics Ultem 2110N PEI
Copyright © lookpolymers.com All Rights Reserved