Manifattura Cattaneo RULON® LR Polytetrafluoroethylene
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE |
| Manufacturer | Manifattura Cattaneo spa |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Manifattura Cattaneo RULON® LR Polytetrafluoroethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.25 g/cc | 0.0813 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.00 % @Temperature 23.0 °C |
0.00 % @Temperature 73.4 °F |
50% RH; ASTM D570 |
| Water Absorption at Saturation | 0.015 % | 0.015 % | ASTM D570 |
| Deformation | 3.0 % @Time 86400 sec, Pressure 100 MPa |
3.0 % @Time 24.0 hour, Pressure 14500 psi |
ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 60 - 65 | 60 - 65 | ASTM D 2240 |
| Tensile Strength at Break | 10.3 MPa | 1490 psi | ASTM D638 |
| Elongation at Break | 150 % | 150 % | ASTM D638 |
| Compressive Yield Strength | 3.60 MPa @Strain 1.00 %, Time 3.60e+6 sec |
522 psi @Strain 1.00 %, Time 1000 hour |
ASTM D695 |
| Compressive Modulus | 0.440 GPa | 63.8 ksi | ASTM D695 |
| Izod Impact, Notched (ISO) | 320 kJ/m² | 152 ft-lb/in² | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | on polished steel; MPC Test |
| Coefficient of Friction, Static | 0.15 | 0.15 | on polished steel; MPC Test |
| K Factor (Wear Factor) | 0.050 | 0.050 | µm/s. PV = 0.1 MPa-m/s; max P = 6.9 MPa; MPC Test |
| Limiting Pressure Velocity | 0.350 MPa-m/sec | 9990 psi-ft/min | without lubrication; MPC Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 106 µm/m-°C @Temperature 23.0 - 100 °C |
58.9 µin/in-°F @Temperature 73.4 - 212 °F |
|
| CTE, linear, Transverse to Flow | 92.0 µm/m-°C @Temperature 23.0 °C |
51.1 µin/in-°F @Temperature 73.4 °F |
|
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | ASTM D177 |
| Maximum Service Temperature, Air | 288 °C | 550 °F | |
| Minimum Service Temperature, Air | -240 °C | -400 °F | |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Surface Resistance | 2.00e+13 ohm | 2.00e+13 ohm | ASTM D257 |
| Dielectric Constant | 2.5 @Frequency 1.00e+6 Hz |
2.5 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 15.7 kV/mm @Thickness 2.00 mm |
399 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dielectric Loss Index | 0.0010 - 0.0040 @Frequency 1.00e+6 Hz |
0.0010 - 0.0040 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| FDA | No | No |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red Rust | |
| UV Resistance | Y |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP FARADEX NX07330 PC+ABS (Asia Pacific)
- Multibase Nylex™ 2185 FR Polyamide + PP
- Magyar Aluminum ALO-P95-01 Alumina
- SABIC Innovative Plastics NORYL WCV065 PPE+Polyolefin
- Zircar Ceramics ASB-2300 Alumina-Silica Blanket
- Dow Corning 2-3422 Antifoam Compound
- BASF Paliogen® Maroon L 3980 Color Additive
- Assab Steels EM33 Steel for Plastic Molds
- AK Steel 17-7 PH® Precipitation Hardening Stainless Steel, Condition TH 1050
- PolyOne Synprene® RT-3850E Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved