- SABIC Innovative Plastics Ultem XH6050M PEI Copolymer (Europe-Africa-Middle East)
SABIC Innovative Plastics Ultem XH6050M PEI Copolymer (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Ultem XH6050M PEI Copolymer (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Enhanced flow Polyetherimidesulfone copolymer (Tg 247C) with internal mold release. ECO Conforming, UL94 V0 listing. Resin is subject to U.S. Commerce Control Laws (15CFR Chapter VII, Part 774).This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D 792 |
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.65 % | 0.65 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.75 % @Temperature 23.0 °C |
1.75 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on tensile bar; SABIC Method |
| 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 360 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 680 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 12.5 g/10 min @Load 6.60 kg, Temperature 367 °C |
12.5 g/10 min @Load 14.6 lb, Temperature 693 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 138 MPa | 20000 psi | ISO 2039-1 |
| Tensile Strength at Break | 78.0 MPa | 11300 psi | 5 mm/min; ISO 527 |
| 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
| 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 16.3 % | 16.3 % | 5 mm/min; ISO 527 |
| 25 % | 25 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 6.0 % | 6.0 % | Type I, 5 mm/min; ASTM D 638 |
| 8.4 % | 8.4 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.12 GPa | 453 ksi | 1 mm/min; ISO 527 |
| 3.51 GPa | 509 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Strength | 123 MPa | 17800 psi | 2 mm/min; ISO 178 |
| 158 MPa | 22900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Yield Strength | 155 MPa | 22500 psi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Flexural Modulus | 3.07 GPa | 445 ksi | 2 mm/min; ISO 178 |
| 3.17 GPa | 460 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.690 J/cm @Temperature 23.0 °C |
1.29 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| 0.740 J/cm @Temperature -30.0 °C |
1.39 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 | |
| Izod Impact, Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 147 kJ/m² @Temperature -30.0 °C |
69.9 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U |
| 196 kJ/m² @Temperature 23.0 °C |
93.3 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Impact Test | 33.0 J @Temperature 23.0 °C |
24.3 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature -40.0 - 150 °C |
27.8 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 50.0 µm/m-°C @Temperature 23.0 - 150 °C |
27.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature -40.0 - 150 °C |
27.8 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 50.0 µm/m-°C @Temperature 23.0 - 150 °C |
27.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| Thermal Conductivity | 0.220 W/m-K | 1.53 BTU-in/hr-ft²-°F | ASTM E 1530 |
| Deflection Temperature at 0.46 MPa (66 psi) | 237 °C @Thickness 6.40 mm |
459 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 228 °C | 442 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 217 °C @Thickness 3.20 mm |
423 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| 230 °C @Thickness 6.40 mm |
446 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 240 °C | 464 °F | Rate B/120; ISO 306 |
| 242 °C | 468 °F | Rate B/50; ASTM D 1525 | |
| 242 °C | 468 °F | Rate B/50; ISO 306 | |
| Glass Transition Temp, Tg | 247 °C | 477 °F | |
| Oxygen Index | 45 % | 45 % | LOI; ISO 4589 |
| Glow Wire Test | 850 °C @Thickness 3.00 mm |
1560 °F @Thickness 0.118 in |
Glow Wire Ignitability Temperature; IEC 60695-2-13 |
| 960 °C @Thickness 3.20 mm |
1760 °F @Thickness 0.126 in |
Glow Wire Flammability Index; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 14.0 kV/mm @Thickness 3.20 mm |
356 kV/in @Thickness 0.126 in |
in oil; ASTM D 149 |
| Dissipation Factor | 0.0010 @Frequency 1000 Hz |
0.0010 @Frequency 1000 Hz |
IEC 60250 |
| 0.0070 @Frequency 1.00e+6 Hz |
0.0070 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.0080 @Frequency 100 Hz |
0.0080 @Frequency 100 Hz |
IEC 60250 | |
| 0.018 @Frequency 50.0 - 60.0 Hz |
0.018 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | Passes | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- NanoAmor 95%; OD: 80-200 nm Carbon Nanofibers
- ExxonMobil 75W-80 Mobilfluid LT
- Diamond Polymers ABS 2512
- ExxonMobil 15W-40 Exxon XD-3 Extra
- Dow Corning 2-8197 EMULSION
- 3M Scotch Pad™ 8327 Custom Carry Handle
- 3M Scotchkote™ HB 850 Epoxy Floor Coating
- Solvay RHODAPEX® ESY/CG Surfactant
- Techmer ES HiFill FR® PA6 GF25 FR 25% Glass Filled
Copyright © lookpolymers.com All Rights Reserved