SABIC Innovative Plastics Ultem AUT230M PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Ultem AUT230M PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Transparent polyetherimide (Tg 247 degC). Contains low level of mold release. Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 230 degC (SABIC Innovative Plastics method).This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D 792 |
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.65 % | 0.65 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.75 % @Temperature 23.0 °C |
1.75 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on tensile bar; SABIC Method |
| 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 360 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 680 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 15.5 g/10 min @Load 6.60 kg, Temperature 367 °C |
15.5 g/10 min @Load 14.6 lb, Temperature 693 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 78.0 MPa | 11300 psi | 5 mm/min; ISO 527 |
| 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
| 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 16.3 % | 16.3 % | 5 mm/min; ISO 527 |
| 25 % | 25 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 6.0 % | 6.0 % | Type I, 5 mm/min; ASTM D 638 |
| 8.4 % | 8.4 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.12 GPa | 453 ksi | 1 mm/min; ISO 527 |
| 3.51 GPa | 509 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 123 MPa | 17800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.07 GPa | 445 ksi | 2 mm/min; ISO 178 |
| 3.17 GPa | 460 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.690 J/cm @Temperature 23.0 °C |
1.29 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| 0.740 J/cm @Temperature -30.0 °C |
1.39 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 | |
| Izod Impact, Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 147 kJ/m² @Temperature -30.0 °C |
69.9 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U |
| 196 kJ/m² @Temperature 23.0 °C |
93.3 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U | |
| Impact Test | 33.0 J @Temperature 23.0 °C |
24.3 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature -40.0 - 150 °C |
27.8 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 50.0 µm/m-°C @Temperature 23.0 - 150 °C |
27.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature -40.0 - 150 °C |
27.8 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 50.0 µm/m-°C @Temperature 23.0 - 150 °C |
27.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 237 °C @Thickness 6.40 mm |
459 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 228 °C | 442 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 217 °C @Thickness 3.20 mm |
423 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| 230 °C @Thickness 6.40 mm |
446 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 240 °C | 464 °F | Rate B/120; ISO 306 |
| 242 °C | 468 °F | Rate B/50; ASTM D 1525 | |
| 242 °C | 468 °F | Rate B/50; ISO 306 | |
| Glass Transition Temp, Tg | 247 °C | 477 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | Passes | IEC 60695-10-2 |
| Metallized Haze Onset, °C | 230 | SABIC Method |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® MG34LGHF ABS
- Shinil Chemical SHINSTRA PA-66 Devlop Structural Polymer Window Strip
- Stellar Canada CERAMITE® BKR-F Wear Resistant Castable
- SABIC Innovative Plastics LNP THERMOCOMP EF006ER PEI (Asia Pacific)
- Master Bond Supreme 10HTCL Epoxy for Cryogenic Applications
- Zotefoams Evazote® EV30 Ethylene Vinyl Acetate Copolymer Foam
- Chosun Refractories SF33 Hard Fireclay brick
- Permabond 792 Cyanoacrylate, Surface insensitive
- Arkema Group Rilsan® BESHV Nylon 11, Blow Molding Grade (Conditioned)
Copyright © lookpolymers.com All Rights Reserved