SABIC Innovative Plastics Ultem ATX103R PEI+PCE (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI) + PCE
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Ultem ATX103R PEI+PCE (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing in recognized colors.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Specific Gravity 1.45 g/cc
1.45 g/cc
ASTM D 792
Density 1.45 g/cc
0.0524 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.12 %
0.12 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.35 %

@Temperature 23.0 °C
 0.35 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
on tensile bar; SABIC Method
0.0020 - 0.0040 cm/cm

@Thickness 3.20 mm
 0.0020 - 0.0040 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0030 - 0.0050 cm/cm

@Thickness 3.20 mm
 0.0030 - 0.0050 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 40 g/10 min

@Load 5.00 kg,
Temperature 360 °C
 40 g/10 min

@Load 11.0 lb,
Temperature 680 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
60 g/10 min

@Load 6.60 kg,
Temperature 337 °C
 60 g/10 min

@Load 14.6 lb,
Temperature 639 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 132 MPa
19100 psi
Type I, 5 mm/min; ASTM D 638
132 MPa
19100 psi
5 mm/min; ISO 527
Tensile Strength, Yield 132 MPa
19100 psi
Type I, 5 mm/min; ASTM D 638
132 MPa
19100 psi
5 mm/min; ISO 527
Elongation at Break 2.5 %
2.5 %
5 mm/min; ISO 527
2.7 %
2.7 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 2.5 %
2.5 %
5 mm/min; ISO 527
2.7 %
2.7 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 8.92 GPa
1290 ksi
1 mm/min; ISO 527
8.97 GPa
1300 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 203 MPa
29400 psi
1.3 mm/min, 50 mm span; ASTM D 790
207 MPa
30000 psi
2 mm/min; ISO 178
Flexural Modulus 8.27 GPa
1200 ksi
1.3 mm/min, 50 mm span; ASTM D 790
8.29 GPa
1200 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.44 J/cm

@Temperature 23.0 °C
 2.70 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 9.08 J/cm

@Temperature 23.0 °C
 17.0 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 8.00 kJ/m²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
9.00 kJ/m²

@Temperature 23.0 °C
 4.28 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 52.0 kJ/m²

@Temperature -30.0 °C
 24.7 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
58.0 kJ/m²

@Temperature 23.0 °C
 27.6 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Charpy Impact Unnotched 6.00 J/cm²

@Temperature 23.0 °C
 28.6 ft-lb/in²

@Temperature 73.4 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eU
6.20 J/cm²

@Temperature -30.0 °C
 29.5 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²

@Temperature 23.0 °C
 4.28 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.900 J/cm²

@Temperature -30.0 °C
 4.28 ft-lb/in²

@Temperature -22.0 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 21.0 J

@Temperature 23.0 °C
 15.5 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 21.0 µm/m-°C

@Temperature -40.0 - 150 °C
 11.7 µin/in-°F

@Temperature -40.0 - 302 °F
 ASTM E 831
21.0 µm/m-°C

@Temperature 23.0 - 150 °C
 11.7 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 63.0 µm/m-°C

@Temperature -40.0 - 150 °C
 35.0 µin/in-°F

@Temperature -40.0 - 302 °F
 ASTM E 831
63.0 µm/m-°C

@Temperature 23.0 - 150 °C
 35.0 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 162 °C
324 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
170 °C

@Thickness 3.20 mm
 338 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
174 °C

@Thickness 6.40 mm
 345 °F

@Thickness 0.252 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 158 °C
316 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
161 °C

@Thickness 3.20 mm
 322 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
165 °C

@Thickness 6.40 mm
 329 °F

@Thickness 0.252 in
 unannealed; ASTM D 648
Vicat Softening Point 176 °C
349 °F
Rate B/50; ISO 306
177 °C
351 °F
Rate B/120; ISO 306
180 °C
356 °F
Rate B/50; ASTM D 1525
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 UL 94
5VA

@Thickness 3.00 mm
 5VA

@Thickness 0.118 in
 UL 94
Electrical Properties Metric English Comments
Volume Resistivity 1.20e+16 ohm-cm
1.20e+16 ohm-cm
IEC 60093
Surface Resistance 2.80e+13 ohm
2.80e+13 ohm
ROA; IEC 60093
Dielectric Strength 22.0 kV/mm

@Thickness 1.60 mm
 559 kV/in

@Thickness 0.0630 in
 in oil; IEC 60243-1
Dissipation Factor 0.0041

@Frequency 50.0 - 60.0 Hz
 0.0041

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.0062

@Frequency 1000 Hz
 0.0062

@Frequency 1000 Hz
 IEC 60250
0.0116

@Frequency 1.00e+6 Hz
 0.0116

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 125 V
125 V
IEC 60112
>= 125 V
>= 125 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Passes
IEC 60695-10-2