Toyobo GLAMIDE® T-656E Nylon-66

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant
Manufacturer	Toyobo
Trade Name	GLAMIDE®
Port	Shanghai port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Toyobo GLAMIDE® T-656E Nylon-66.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-656E is a non-reinforced Nylon-66 with high abrasion resistance.

Physical Properties	Metric	English	Comments
Specific Gravity	1.12 g/cc	1.12 g/cc	Absolute Drying; ASTM-D792
Water Absorption	1.1 %	1.1 %	Absolute Drying; ASTM-D570
Moisture Absorption at Equilibrium	2.4 %	2.4 %	Absolute Drying; ASTM-D570
Linear Mold Shrinkage	0.0060 - 0.012 cm/cm <br>@Thickness 1.00 mm	0.0060 - 0.012 in/in <br>@Thickness 0.0394 in	Absolute Drying
	0.015 - 0.022 cm/cm <br>@Thickness 3.00 mm	0.015 - 0.022 in/in <br>@Thickness 0.118 in	Absolute Drying

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	118	118	Absolute Drying; ASTM-D785
Tensile Strength, Ultimate	24.0 MPa <br>@Temperature 80.0 °C	3480 psi <br>@Temperature 176 °F	Practical Use (Water Absorption 2.4%); ASTM-D638
	30.0 MPa <br>@Temperature 80.0 °C	4350 psi <br>@Temperature 176 °F	Absolute Drying; ASTM-D638
	45.0 MPa <br>@Temperature 23.0 °C	6530 psi <br>@Temperature 73.4 °F	Practical Use (Water Absorption 2.4%); ASTM-D638
	70.0 MPa <br>@Temperature 23.0 °C	10200 psi <br>@Temperature 73.4 °F	Absolute Drying; ASTM-D638
	90.0 MPa <br>@Temperature -40.0 °C	13100 psi <br>@Temperature -40.0 °F	Practical Use (Water Absorption 2.4%); ASTM-D638
	95.0 MPa <br>@Temperature -40.0 °C	13800 psi <br>@Temperature -40.0 °F	Absolute Drying; ASTM-D638
Elongation at Break	52 %	52 %	Absolute Drying; ASTM-D638
	>= 200 %	>= 200 %	Practical Use (Water Absorption 2.4%); ASTM-D638
Flexural Strength	38.0 MPa <br>@Temperature 80.0 °C	5510 psi <br>@Temperature 176 °F	Practical Use (Water Absorption 2.4%); ASTM-D790
	50.0 MPa <br>@Temperature 80.0 °C	7250 psi <br>@Temperature 176 °F	Absolute Drying; ASTM-D790
	70.0 MPa <br>@Temperature 23.0 °C	10200 psi <br>@Temperature 73.4 °F	Practical Use (Water Absorption 2.4%); ASTM-D790
	96.0 MPa <br>@Temperature 23.0 °C	13900 psi <br>@Temperature 73.4 °F	Absolute Drying; ASTM-D790
	115 MPa <br>@Temperature -40.0 °C	16700 psi <br>@Temperature -40.0 °F	Practical Use (Water Absorption 2.4%); ASTM-D790
	125 MPa <br>@Temperature -40.0 °C	18100 psi <br>@Temperature -40.0 °F	Absolute Drying; ASTM-D790
Flexural Modulus	0.400 GPa <br>@Temperature 80.0 °C	58.0 ksi <br>@Temperature 176 °F	Practical Use (Water Absorption 2.4%); ASTM-D790
	0.800 GPa <br>@Temperature 80.0 °C	116 ksi <br>@Temperature 176 °F	Absolute Drying; ASTM-D790
	1.30 GPa <br>@Temperature 23.0 °C	189 ksi <br>@Temperature 73.4 °F	Practical Use (Water Absorption 2.4%); ASTM-D790
	2.70 GPa <br>@Temperature 23.0 °C	392 ksi <br>@Temperature 73.4 °F	Absolute Drying; ASTM-D790
	2.90 GPa <br>@Temperature -40.0 °C	421 ksi <br>@Temperature -40.0 °F	Practical Use (Water Absorption 2.4%); ASTM-D790
	3.10 GPa <br>@Temperature -40.0 °C	450 ksi <br>@Temperature -40.0 °F	Absolute Drying; ASTM-D790
Izod Impact, Notched	1.00 J/cm <br>@Temperature -40.0 °C	1.87 ft-lb/in <br>@Temperature -40.0 °F	Absolute Drying; ASTM-D256
	1.30 J/cm <br>@Temperature -40.0 °C	2.44 ft-lb/in <br>@Temperature -40.0 °F	Practical Use (Water Absorption 2.4%); ASTM-D256
	1.45 J/cm <br>@Temperature 23.0 °C	2.72 ft-lb/in <br>@Temperature 73.4 °F	Absolute Drying; ASTM-D256
	>= 4.00 J/cm <br>@Temperature 23.0 °C	>= 7.49 ft-lb/in <br>@Temperature 73.4 °F	Practical Use (Water Absorption 2.4%); ASTM-D256
Taber Abrasion, mg/1000 Cycles	<= 5.0	<= 5.0	CS-17, Absolute Drying; ASTM-D1044

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	215 °C	419 °F	Absolute Drying; ASTM-D648
Deflection Temperature at 1.8 MPa (264 psi)	68.0 °C	154 °F	Absolute Drying; ASTM-D648
Flammability, UL94	HB	HB

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+9 - 1.00e+10 ohm-cm	1.00e+9 - 1.00e+10 ohm-cm	Practical Use (Water Absorption 2.4%); ASTM-D257
	1.00e+12 ohm-cm	1.00e+12 ohm-cm	Absolute Drying; ASTM-D257
Dielectric Strength	14.0 kV/mm <br>@Thickness 2.00 mm	356 kV/in <br>@Thickness 0.0787 in	Practical Use (Water Absorption 2.4%); ASTM-D149
	21.0 kV/mm <br>@Thickness 2.00 mm	533 kV/in <br>@Thickness 0.0787 in	Absolute Drying; ASTM-D149
Arc Resistance	110 sec	110 sec	Practical Use (Water Absorption 2.4%); ASTM-D495
	120 sec	120 sec	Absolute Drying; ASTM-D495
Comparative Tracking Index	>= 600 V	>= 600 V	IEC Method

Processing Properties	Metric	English
Melt Temperature	270 - 290 °C	518 - 554 °F
Mold Temperature	40.0 - 80.0 °C	104 - 176 °F
Injection Pressure	30.0 - 40.0 MPa	4350 - 5800 psi