SABIC Innovative Plastics Ultem 2210K PEI (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Ultem 2210K PEI (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D 792 |
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.55 % | 0.55 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.0 % @Temperature 23.0 °C |
1.0 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 13 g/10 min @Load 6.60 kg, Temperature 337 °C |
13 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D 1238 |
| 16 g/10 min @Load 5.00 kg, Temperature 360 °C |
16 g/10 min @Load 11.0 lb, Temperature 680 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 139 MPa | 20200 psi | Type I, 5 mm/min; ASTM D 638 |
| 140 MPa | 20300 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 139 MPa | 20200 psi | Type I, 5 mm/min; ASTM D 638 |
| 140 MPa | 20300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D 638 |
| 5.0 % | 5.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D 638 |
| 5.0 % | 5.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 6.80 GPa | 986 ksi | 1 mm/min; ISO 527 |
| 6.89 GPa | 999 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 210 MPa | 30500 psi | 2 mm/min; ISO 178 |
| 227 MPa | 32900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 6.50 GPa | 943 ksi | 2 mm/min; ISO 178 |
| 6.89 GPa | 999 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.640 J/cm @Temperature 23.0 °C |
1.20 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| 0.640 J/cm @Temperature -30.0 °C |
1.20 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 | |
| Izod Impact, Unnotched | 4.75 J/cm @Temperature 23.0 °C |
8.90 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Charpy Impact, Notched | 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Impact Test | 13.0 J @Temperature 23.0 °C |
9.59 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature -40.0 - 150 °C |
13.9 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 25.0 µm/m-°C @Temperature 23.0 - 150 °C |
13.9 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature -40.0 - 150 °C |
33.3 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 60.0 µm/m-°C @Temperature 23.0 - 150 °C |
33.3 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C @Thickness 6.40 mm |
410 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 209 °C @Thickness 3.20 mm |
408 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| 211 °C @Thickness 6.40 mm |
412 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 212 °C | 414 °F | Rate B/50; ISO 306 |
| 218 °C | 424 °F | Rate B/120; ISO 306 | |
| 225 °C | 437 °F | Rate B/50; ASTM D 1525 | |
| Glass Transition Temp, Tg | 217 °C | 423 °F |
Users viewing this material also viewed the following:
- Ovation Polymers Nima™ HL 30530 GF FR PET, 30% Glass Fiber
- Heatbath/Park Marquench Quenching and Tempering Salt
- Stir SpA T 4599 A MOD (PVC)
- Schmolz + Bickenbach MoldMAX® V Copper Alloy
- Lubrizol Estane® ALR CL60D Thermoplastic Polyurethane
- Alliance Polymers Zythane™ 6055D Thermoplastic Polyurethane Elastomer
- ConocoPhillips 32 Transparent Cutting Oil
- LATI Latilub 66-01M PA66, Molybdenum disulphide Filled
- Sumitomo Bakelite North America FM 4017F Fiberglass and Mineral Reinforced Phenolic
Copyright © lookpolymers.com All Rights Reserved