SABIC Innovative Plastics LNP THERMOCOMP ZFM62P PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP ZFM62P PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* ZFM62P is a compound based on PPE+PS resin containing 10% Glass Fiber, 30% Mical. Added features of this material include: Exceptional Processing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0800 % | 0.0800 % | 50% RH, 24 hrs; ASTM D570 |
| 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0045 cm/cm @Time 86400 sec |
0.0045 in/in @Time 24.0 hour |
ISO 294 |
| 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 66.0 MPa | 9570 psi | ISO 527 |
| 75.0 MPa | 10900 psi | ASTM D638 | |
| Elongation at Break | 1.0 % | 1.0 % | ISO 527 |
| 1.4 % | 1.4 % | ASTM D638 | |
| Tensile Modulus | 8.54 GPa | 1240 ksi | 1 mm/min; ISO 527 |
| 8.97 GPa | 1300 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 |
| 124 MPa | 18000 psi | ASTM D790 | |
| Flexural Modulus | 8.69 GPa | 1260 ksi | ISO 178 |
| 8.74 GPa | 1270 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.310 J/cm | 0.581 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.92 J/cm | 3.60 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J | 5.16 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 37.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 37.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 35.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 35.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C | 282 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 137 °C @Thickness 3.20 mm |
279 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Indium Corp. Indalloy® 238 Sn-Au Solder Alloy
- SABIC Innovative Plastics ULTEM 1000E PEI (Europe-Africa-Middle East)
- SABIC Innovative Plastics NORYL GFN1 PPE+HIPS (Europe-Africa-Middle East)
- Williams Advanced Alloys WS286 Solder
- Crucible Steel 23-8N Martensitic Steel
- Asahi Kasei Leona® 93G33 33% Glass Filled Nylon 66
- Ashley Polymers Ashlene® R3144 PC/PBT
- PolyOne Stat-Tech™ UR-7SS-5GF/000 PT GY Thermoplastic Elastomer - TPU, Glass Filled (discontinued **)
- Gromax CFG30-QN11N1 Nylon 6 30% Glass Filled (Dry)
- Lubrizol ESTANE® 58311 Ether Based Thermoplastic Polyurethane
Copyright © lookpolymers.com All Rights Reserved