SABIC Innovative Plastics Ultem 1010KM PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Ultem 1010KM PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D 792 |
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.70 % | 0.70 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.25 % @Temperature 23.0 °C |
1.25 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on tensile bar; SABIC Method |
| 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 17.8 g/10 min @Load 6.60 kg, Temperature 337 °C |
17.8 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D 1238 |
| 25 g/10 min @Load 5.00 kg, Temperature 360 °C |
25 g/10 min @Load 11.0 lb, Temperature 680 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa | 12300 psi | 5 mm/min; ISO 527 |
| 105 MPa | 15200 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
| 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 60 % | 60 % | Type I, 5 mm/min; ASTM D 638 |
| 60 % | 60 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 6.0 % | 6.0 % | 5 mm/min; ISO 527 |
| 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 3.30 GPa | 479 ksi | 1 mm/min; ISO 527 |
| 3.59 GPa | 521 ksi | 5 mm/min; ASTM D 638 | |
| Flexural Yield Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 |
| 165 MPa | 23900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 3.30 GPa | 479 ksi | 2 mm/min; ISO 178 |
| 3.52 GPa | 511 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.320 J/cm @Temperature 23.0 °C |
0.599 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| 0.350 J/cm @Temperature -30.0 °C |
0.656 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 | |
| 14.95 J/cm @Thickness 3.20 mm |
28.01 ft-lb/in @Thickness 0.126 in |
reverse notched; ASTM D 256 | |
| Izod Impact, Unnotched | 13.35 J/cm @Temperature 23.0 °C |
25.01 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Impact Test | 33.0 J @Temperature 23.0 °C |
24.3 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 23.0 - 150 °C |
27.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| 55.0 µm/m-°C @Temperature -40.0 - 150 °C |
30.6 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature 23.0 - 150 °C |
27.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| 55.0 µm/m-°C @Temperature -40.0 - 150 °C |
30.6 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 | |
| Thermal Conductivity | 0.220 W/m-K | 1.53 BTU-in/hr-ft²-°F | ASTM C 177 |
| 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | ISO 8302 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 195 °C | 383 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf | |
| 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| 207 °C @Thickness 6.40 mm |
405 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 192 °C | 378 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | |
| 197 °C @Thickness 3.20 mm |
387 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| 199 °C @Thickness 6.40 mm |
390 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 211 °C | 412 °F | Rate B/50; ISO 306 |
| 212 °C | 414 °F | Rate B/120; ISO 306 | |
| 215 °C | 419 °F | Rate A/50; ISO 306 | |
| 219 °C | 426 °F | Rate B/50; ASTM D 1525 | |
| Glass Transition Temp, Tg | 217 °C | 423 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | Passes | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Huntsman AroCy B-10 Monomeric Bisphenol-A Dicyanate
- Fujipoly Industries Sarcon® 30GHR Thin-Film GHR
- GEHR Plastics PA 6.6-30GF Nylon 6.6, 30% Glass Fiber, Conditioned
- SABIC Innovative Plastics LNP THERMOCOMP AFB42 ABS
- SK Chemicals SKYTHANE® 870A T series Polyurethane
- ChevronTexaco Delo® NLGI 00 Grease EP
- ConocoPhillips 2 Bentone Grease NLGI No. 2
- Axiall 4590 Flexible PVC
- Breplast Bretene SP Polypropylene / Polyethylene Composite
- Special Metals UDIMET® alloy L-605 Co-Cr-W-Ni Alloy
Copyright © lookpolymers.com All Rights Reserved