SABIC Innovative Plastics ULTEM LTX300B PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM LTX300B PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Standard flow Polyetherimide blend with low toxicity, smoke, and flame evolution. ECO Compliant, UL94 V0 listing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Halogen Content | 0.00 % | 0.00 % | SABIC Method |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 1.6 g/10 min @Load 6.60 kg, Temperature 295 °C |
1.6 g/10 min @Load 14.6 lb, Temperature 563 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 88 % | 88 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.34 GPa | 484 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 141 MPa | 20500 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Yield Strength | 144 MPa | 20900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 3.20 GPa | 464 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| 21.36 J/cm @Thickness 3.20 mm |
40.02 ft-lb/in @Thickness 0.126 in |
ASTM D256 | |
| Gardner Impact | 35.0 J | 25.8 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C @Thickness 6.40 mm |
374 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 140 °C | 284 °F | UL 746B |
| UL RTI, Mechanical with Impact | 115 °C | 239 °F | UL 746B |
| UL RTI, Mechanical without Impact | 140 °C | 284 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 0.760 mm |
V-0 @Thickness 0.0299 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PE 4020R (20405) Linear Low Density Polyethylene
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR Suprex Clay Filler
- UBE UBEPOL VCR406 Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
- UBE UBESTA® 3035LU1 Rigid Piping Grade Nylon 12
- Chesterton ARC 10 Paste grade machinable composite
- Cotronics Duralco™ 4525 Electrically Resistant, Room Temperature Curing Epoxy
- ExxonMobil 103 Mobilgrease XHP Series
- Dow Engage® 8180 Polyolefin Elastomer
- Fainplast Compounds GA 80 Flexible PVC, Flame Retardant Sheathing
- ExxonMobil HD 7845.30 MMW Blown Film Resin
Copyright © lookpolymers.com All Rights Reserved