- SABIC Innovative Plastics ULTEM HU1110 PEI
SABIC Innovative Plastics ULTEM HU1110 PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM HU1110 PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant. EtO and steam sterilizable. NSF 51 listing, compliant in recognized colors.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ASTM D792 |
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.650 % | 0.650 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.2 % | 1.2 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 16 g/10 min @Load 6.60 kg, Temperature 337 °C |
16 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Melt Index of Compound | 21 g/10 min @Load 5.00 kg, Temperature 360 °C |
21 g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa | 12300 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 |
| 110 MPa | 16000 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 60 % | 60 % | 5 mm/min; ISO 527 |
| 70 % | 70 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 6.0 % | 6.0 % | 5 mm/min; ISO 527 |
| 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 3.50 GPa | 508 ksi | 1 mm/min; ISO 527 |
| 3.72 GPa | 540 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 140 MPa | 20300 psi | 2 mm/min; ISO 178 |
| 165 MPa | 23900 psi | 2.6 mm/min, 100 mm span; ASTM D790 | |
| 174 MPa | 25200 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 3.30 GPa | 479 ksi | 2 mm/min; ISO 178 |
| 3.42 GPa | 496 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| 3.72 GPa | 540 ksi | 2.6 mm/min, 100 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.560 J/cm | 1.05 ft-lb/in | ASTM D256 |
| 19.22 J/cm @Thickness 3.20 mm |
36.01 ft-lb/in @Thickness 0.126 in |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Gardner Impact | 23.0 J | 17.0 ft-lb | ASTM D3029 |
| Dart Drop, Total Energy | 28.0 J @Temperature 23.0 °C |
20.7 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 55.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 55.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 55.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 55.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 198 °C @Thickness 6.40 mm |
388 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 200 °C | 392 °F | Rate B/50; ISO 306 |
| 205 °C | 401 °F | Rate B/120; ISO 306 | |
| 219 °C | 426 °F | Rate B/50; ASTM D1525 | |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| UL RTI, Electrical | 170 °C | 338 °F | UL 746B |
| UL RTI, Mechanical with Impact | 170 °C | 338 °F | UL 746B |
| UL RTI, Mechanical without Impact | 170 °C | 338 °F | UL 746B |
| Flammability, UL94 | V-2 @Thickness 0.710 mm |
V-2 @Thickness 0.0280 in |
UL 94 |
| V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
UL 94 | |
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH GF3050 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
- Huntsman HY 9130 Polyamide
- Lord Adhesives Flocklok® Catalyst 6
- SABIC Innovative Plastics PC2800 PC (Europe-Africa-Middle East)
- Silikony Polskie Gumosil M Silicone Rubber
- Goodfellow Aluminum 65.7/Silicon 34.3 Alloy
- Toyobo Vylopet® EMC310K Glass Reinforced Polyester, Easy Molding Grade
- Formosa Plastics Formolon® 685 PVC
- Arlon LW202Bxx-P1 0.020" (0.508 mm) Self-Fusing Silicone Tape (Triangular, Unsupported) with Poly Interleave
Copyright © lookpolymers.com All Rights Reserved