Eurotec® Tecomid® NA40 NL IX PA6.6, impact modified, natural
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Eurotec |
| Trade Name | Tecomid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecomid® NA40 NL IX PA6.6, impact modified, natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Moisture Absorption | 2.20 % @Temperature 23.0 °C |
2.20 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | Eurotec |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in | Eurotec |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | ISO 527 |
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 18.0 kJ/m² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 262 °C | 504 °F | [10 K/min], ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 260 - 280 °C | 500 - 536 °F | |
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Throat |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | ISO 960 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Medium-Fast |
Users viewing this material also viewed the following:
- Gouda Vuurvast CURON 150 HS Dense Refractory Castable
- Michelman® Michem® Lube 270R Anionic paraffin/polyethylene wax emulsion
- Loxim 210 01HB Polybutylene Terephthalate
- ITW Devcon Flexane® Rubber Repair / Castable Urethane Belt Repair Kit, Black
- H.C. Starck 2702 Molybdenum Alloy P/M - TZM Sheet
- SK Chemicals SKYTHANE® US210 Magnetic Binder
- A. Schulman SCHULAMID® 6 GB30 30% Glass Bead Reinforced Nylon 6
- DuPont Performance Polymers Delrin® 300PE NC010A Acetal Homopolymer
- Kraton® G1726 M (SEBS) Linear Triblock Copolymer
- DuPont™ Sclairfilm® SL-3 LLDPE Film, Laminating, 50.8 µm Thickness (discontinued **)
Copyright © lookpolymers.com All Rights Reserved