SABIC Innovative Plastics ULTEM HU1000 PEI (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM HU1000 PEI (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Transparent, standard flow Polyetherimide (Tg 217C). RoHS compliant. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant. UL94 V0 and 5VA listed. EtO and steam sterilizable.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Water Absorption | 0.25 % @Time 86400 sec |
0.25 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption | 0.700 % | 0.700 % | 23°C / 50% RH; ISO 62 |
| Moisture Absorption at Equilibrium | 1.25 % | 1.25 % | ASTM D570 |
| Water Absorption at Saturation | 1.25 % | 1.25 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 9.0 g/10 min @Load 6.60 kg, Temperature 337 °C |
9.0 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Melt Index of Compound | 13 g/10 min @Load 5.00 kg, Temperature 220 °C |
13 g/10 min @Load 11.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa | 12300 psi | 5 mm/min; ISO 527 |
| 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
| 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 60 % | 60 % | Type I, 5 mm/min; ASTM D638 |
| 60 % | 60 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 6.0 % | 6.0 % | 5 mm/min; ISO 527 |
| 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 3.20 GPa | 464 ksi | 1 mm/min; ISO 527 |
| 3.58 GPa | 519 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 |
| 173 MPa | 25100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 3.30 GPa | 479 ksi | 2 mm/min; ISO 178 |
| 3.43 GPa | 497 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| 0.550 J/cm @Temperature -30.0 °C |
1.03 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 13.35 J/cm | 25.01 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 55.8 µm/m-°C @Temperature -20.0 - 150 °C |
31.0 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 54.0 µm/m-°C @Temperature -20.0 - 150 °C |
30.0 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 201 °C @Thickness 6.40 mm |
394 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 211 °C | 412 °F | Rate B/120; ISO 306 |
| 215 °C | 419 °F | Rate B/50; ISO 306 | |
| 218 °C | 424 °F | Rate B/50; ASTM D1525 | |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| Oxygen Index | 47 % | 47 % | ASTM D2863 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.15 @Frequency 1000 Hz |
3.15 @Frequency 1000 Hz |
ASTM D150 |
| Dielectric Strength | 27.9 kV/mm @Thickness 1.60 mm |
709 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 |
| 32.7 kV/mm @Thickness 1.60 mm |
831 kV/in @Thickness 0.0630 in |
in air; ASTM D149 | |
| Dissipation Factor | 0.0013 @Frequency 1000 Hz |
0.0013 @Frequency 1000 Hz |
ASTM D150 |
| 0.0025 @Frequency 2.45e+9 Hz |
0.0025 @Frequency 2.45e+9 Hz |
ASTM D150 | |
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| NBS Smoke Density, Flaming, Ds 4 min | 0.7 | ASTM E 662 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® LGN2000 PC (Asia Pacific)
- RheTech Products M12P256-01 12% Mica Reinforced Polypropylene Copolymer, Black
- Mitsubishi Xantar® 19 R Polycarbonate
- SABIC Innovative Plastics LNP THERMOCOMP PF009 PA 6 (Asia Pacific)
- Tisan TISOPLEN® 20% Calcite Filled Heat Stabilized Copolymer Polypropylene
- DuPont Performance Polymers Crastin® LW9030FR NC010 PBT+ASA (Unverified Data**)
- BASF Sicotan® Yellow L 1010 Color Additive
Copyright © lookpolymers.com All Rights Reserved