Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
Manufacturer | SABIC Innovative Plastics (GE Plastics) |
Trade Name | ULTEM |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | SABIC Innovative Plastics ULTEM CRS5311 PEI.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 |
Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
Melt Flow | 4.0 g/10 min @Load 6.60 kg, Temperature 337 °C |
4.0 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 165 MPa | 23900 psi | Type I, 5 mm/min; ASTM D638 |
Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
Tensile Modulus | 8.96 GPa | 1300 ksi | 5 mm/min; ASTM D638 |
Flexural Yield Strength | 234 MPa | 33900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
Flexural Modulus | 8.96 GPa | 1300 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
1.60 J/cm | 3.00 ft-lb/in | natural, tints; ASTM D256 | |
5.07 J/cm @Thickness 3.20 mm |
9.50 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 218 °C @Thickness 6.40 mm |
424 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
Glass Transition Temp, Tg | 225 °C | 437 °F | |
UL RTI, Electrical | 105 °C | 221 °F | UL 746B |
UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
UL RTI, Mechanical without Impact | 105 °C | 221 °F | UL 746B |
Flammability, UL94 | V-0 @Thickness 1.47 mm |
V-0 @Thickness 0.0579 in |
UL 94 |
5VA @Thickness 1.47 mm |
5VA @Thickness 0.0579 in |
UL 94 |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | UL 746A |
High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | UL 746A |