Samsung Cheil Industries Infino® LF-1030 PC, Unreinforced Anti-Abrasion
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® LF-1030 PC, Unreinforced Anti-Abrasion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Melt Flow | 26 g/10 min @Load 10.0 kg, Temperature 250 °C |
26 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 56.9 MPa | 8250 psi | 50 mm/min; ASTM D638 |
| Flexural Strength | 83.4 MPa | 12100 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.06 GPa | 299 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 6.57 J/cm @Thickness 3.17 mm |
12.3 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 145 °C | 293 °F | B/50; ISO R306 |
Users viewing this material also viewed the following:
- Polimeros Mexicanos Rotolene® Industrial Black Linear Medium Density Polyethylene
- NIZHNEKAMSKNEFTEKHIM PE 4116N (16401) Linear Low Density Polyethylene
- SABIC Innovative Plastics Lexan® 925A PC (Asia Pacific)
- Overview of materials for Thermoplastic Polyimide, Unfilled
- Kraton® D1118 A (SBS) Diblock Copolymer
- Techmer ES HiFill FR® PC GF10 FR BK 10% Glass Filled
- Universal Wire Works AMS 4764 Silver Brazing Filler Metal
- A. Schulman POLYBATCH™ White 8153/UV2 Concentrate Based In Polyethylene
- Chesterton ARC 897 Fine Grade Sliding Wear Compound
- Chang Chun Plastic PBT4830 Fire Retardant & 30% Glass Fiber Enforced Grade PBT
Copyright © lookpolymers.com All Rights Reserved