SABIC Innovative Plastics ULTEM AUT230 PEI (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM AUT230 PEI (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Transparent polyetherimide (Tg 247 degC). Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 230 degC (SABIC Innovative Plastics method). Resin is subject to U.S. Commerce Control Laws (15CFR Chapter VII, Part 774).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.600 % | 0.600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.75 % | 1.75 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on Tensile Bar; SABIC Method |
| 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 15.5 g/10 min @Load 6.60 kg, Temperature 367 °C |
15.5 g/10 min @Load 14.6 lb, Temperature 693 °F |
ASTM D1238 |
| Melt Index of Compound | 8.0 g/10 min @Load 5.00 kg, Temperature 360 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 78.0 MPa | 11300 psi | 5 mm/min; ISO 527 |
| 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
| 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 16.8 % | 16.8 % | 5 mm/min; ISO 527 |
| 25 % | 25 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 6.0 % | 6.0 % | Type I, 5 mm/min; ASTM D638 |
| 8.5 % | 8.5 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.11 GPa | 451 ksi | 1 mm/min; ISO 527 |
| 3.51 GPa | 509 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 123 MPa | 17800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.08 GPa | 447 ksi | 2 mm/min; ISO 178 |
| 3.17 GPa | 460 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| 0.740 J/cm @Temperature -30.0 °C |
1.39 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Dart Drop, Total Energy | 33.0 J @Temperature 23.0 °C |
24.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature -40.0 - 150 °C |
27.8 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 50.0 µm/m-°C @Temperature 23.0 - 150 °C |
27.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature -40.0 - 150 °C |
27.8 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 50.0 µm/m-°C @Temperature 23.0 - 150 °C |
27.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 237 °C @Thickness 6.40 mm |
459 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 228 °C | 442 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 217 °C @Thickness 3.20 mm |
423 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 230 °C @Thickness 6.40 mm |
446 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 238 °C | 460 °F | Rate B/120; ISO 306 |
| 242 °C | 468 °F | Rate B/50; ASTM D1525 | |
| 242 °C | 468 °F | Rate B/50; ISO 306 | |
| Glass Transition Temp, Tg | 247 °C | 477 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | Passes | IEC 60695-10-2 |
| Metallized Haze Onset | 230°C | SABIC Method |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Packaging PK8 WHITE 1081 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Plastcom SLOVASTER® B1 GF 10 PBT, 10% glass fibre
- Nilit FRIANYL B63 W-KF30 Nylon 6 for injection molding, 30% short glass fiber reinforced
- Invista T 94 PET Copolymer Packaging Resin (discontinued **)
- Fiberfil® J-60/20/FR Polypropylene Homopolymer, 20% Glass Reinforced, Flame Retardant
- Lucent Polymers GPP-230 Polypropylene, 30% Glass Fiber Reinforced, Chemically Coupled, Impact Modified
- Lucite International Colacryl ® 1207 Acrylic Solution Resin
- SGL Carbon Group EK 2240 Carbon Graphite
- Zeon Chemicals Nipol® 1034-60 Nitrile Elastomer
- Abatron AboCoat 8709-10 Silver-Filled Electrically Conductive Acrylic Compound
Copyright © lookpolymers.com All Rights Reserved