| Peel Strength |
0.07669 kN/m |
0.4375 pli |
HD Polyethylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.0877 kN/m |
0.500 pli |
LD Polyethylene, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.0877 kN/m |
0.500 pli |
LD Polyethylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.09861 kN/m |
0.5625 pli |
HD Polyethylene, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.1205 kN/m |
0.6875 pli |
Polypropylene, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.131 kN/m |
0.750 pli |
HD Polyethylene, 90° Peel, Conditioned for 3 days at 70°C; ASTM D3330 |
| |
0.131 kN/m |
0.750 pli |
LD Polyethylene, 90° Peel, Conditioned for 3 days at 70°C; ASTM D3330 |
| |
0.1424 kN/m |
0.8125 pli |
LD Polyethylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.153 kN/m |
0.875 pli |
Polypropylene, 90° Peel, Conditioned for 3 days at 70°C; ASTM D3330 |
| |
0.153 kN/m |
0.875 pli |
Polypropylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.1643 kN/m |
0.9375 pli |
HD Polyethylene, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.175 kN/m |
1.00 pli |
Polypropylene, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.1972 kN/m |
1.125 pli |
LDPE, 180° Peel, Conditioned for 3 days at 70°C; ASTM D3330 |
| |
0.20817 kN/m |
1.1875 pli |
HDPE, 180° Peel, Conditioned for 3 days at 70°C; ASTM D3330 |
| |
0.20817 kN/m |
1.1875 pli |
Polycarbonate 90° Peel, Conditioned for 3 days at 70°C; ASTM D3330 |
| |
0.23008 kN/m |
1.3125 pli |
HD Polyethylene, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.23008 kN/m |
1.3125 pli |
LD Polyethylene, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.23008 kN/m |
1.3125 pli |
LD Polyethylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.2410 kN/m |
1.375 pli |
Polypropylene, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.25199 kN/m |
1.4375 pli |
LD Polyethylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.27391 kN/m |
1.5625 pli |
Polypropylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.27391 kN/m |
1.5625 pli |
HD Polyethylene, 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.27391 kN/m |
1.5625 pli |
HD Polyethylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.2849 kN/m |
1.625 pli |
Polypropylene, 180° Peel, Conditioned for 3 days at 70°C; ASTM D3330 |
| |
0.3287 kN/m |
1.875 pli |
Polypropylene, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.3725 kN/m |
2.125 pli |
Glass, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.38347 kN/m |
2.1875 pli |
Stainless Steel, 90° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.4163 kN/m |
2.375 pli |
Stainless Steel, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.4163 kN/m |
2.375 pli |
Polycarbonate 90° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.44921 kN/m |
2.5625 pli |
Glass, 180° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.44921 kN/m |
2.5625 pli |
Glass, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.49303 kN/m |
2.8125 pli |
Glass, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.5040 kN/m |
2.875 pli |
Polycarbonate 180° Peel, Initial, 10 min dwell at RT; ASTM D3330 |
| |
0.5040 kN/m |
2.875 pli |
Stainless Steel, 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.526 kN/m |
3.00 pli |
Polycarbonate 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.526 kN/m |
3.00 pli |
Glass, 90° Peel, Conditioned for 3 days at 70°C; ASTM D3330 |
| |
0.526 kN/m |
3.00 pli |
Polycarbonate 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.53686 kN/m |
3.0625 pli |
Stainless Steel, 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.53686 kN/m |
3.0625 pli |
Stainless Steel, 90° Peel, Conditioned for 3 days at 70°C; ASTM D3330 |
| |
0.5478 kN/m |
3.125 pli |
Glass, 180° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.5478 kN/m |
3.125 pli |
Glass, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.5478 kN/m |
3.125 pli |
Polycarbonate 90° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |
| |
0.58068 kN/m |
3.3125 pli |
Stainless Steel, 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.58068 kN/m |
3.3125 pli |
Polycarbonate 90° Peel, Conditioned for 3 days at RT; ASTM D3330 |
| |
0.6793 kN/m |
3.875 pli |
Stainless Steel, 180° Peel, Conditioned for 24 hrs at 32°C at 90% RH; ASTM D3330 |