Sax Polymers SAXALEN PPH327G28 Polypropylene Homopolymer, 28% Glass Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Sax Polymers |
| Trade Name | SAXALEN |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXALEN PPH327G28 Polypropylene Homopolymer, 28% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXALEN PPH327G28 is a 28% glass filled Polypropylene - Homopolymer injection molding grade with increased stiffness.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 g/10 min @Load 4.76 lb, Temperature 446 °F |
from MVR; ISO 1033 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 84.0 MPa | 12200 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 6.00 GPa | 870 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 118 MPa | 17100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.60 GPa | 667 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 9.00 kJ/m² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 41.0 kJ/m² @Temperature -30.0 °C |
19.5 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 44.0 kJ/m² @Temperature 23.0 °C |
20.9 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 135 °C | 275 °F | B/120; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 250 °C | 428 - 482 °F | |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F |
Users viewing this material also viewed the following:
- Global GA-2850 High Density Polyethylene, Blow Molding Grade (discontinued **)
- Kazanorgsintez 102-21 Composition of Low Density Polyethylene, Crack-Proof
- Saint-Gobain CHR® SG15-06(R) High Performance Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- A. Schulman LP479-01 High-Density Polyethylene Homopolymer
- A. Schulman POLYBATCH™ Dark Blue Oil LL40350/4 Concentrate Based In LLDPE
- Toyobo TS201 PPS, Glass Fiber/Mineral Reinforced
- Dow Corning 7-3123 MANGO BLEND EMULSION
- Cytec Thornel® VCB-20 Carbon Fiber Cloth
- Aaron Industries AAROLENE® ARPS 100-1 GPPS BLACK Polystyrene Compounded Resin
- BASF Dimethyldicykan 3,3’-Dimethyl-4,4’-diamino-dicyclohexylmethane
Copyright © lookpolymers.com All Rights Reserved