SABIC Innovative Plastics ULTEM 1010M PEI (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Shanghai port, China
Download PDF SABIC Innovative Plastics ULTEM 1010M PEI (Europe-Africa-Middle East).pdf
Price EMAIL US  sales@lookpolymers.com
Material Notes:
Enhanced flow Polyetherimide (Tg 217C) with internal mold release. Resin is RoHS compliant.
Mechanical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ISO 1183
Moisture Absorption 0.700 %
0.700 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 1.25 %
1.25 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 in/in
on Tensile Bar; SABIC Method
Melt Index of Compound 13 g/10 min
<br>@Load 5.00 kg,<br> Temperature 340 °C
 13 g/10 min
<br>@Load 11.0 lb,<br> Temperature 644 °F
 MVR [cm^3/10 min]; ISO 1133
Thermal Properties Metric English Comments
Hardness, H358/30 140 MPa
20300 psi
ISO 2039-1
Tensile Strength at Break 85.0 MPa
12300 psi
50 mm/min; ISO 527
Tensile Strength, Yield 105 MPa
15200 psi
50 mm/min; ISO 527
Elongation at Break 60 %
60 %
50 mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 3.30 GPa
479 ksi
1 mm/min; ISO 527
Flexural Yield Strength 160 MPa
23200 psi
2 mm/min; ISO 178
Flexural Modulus 3.30 GPa
479 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
5.00 kJ/m²
<br>@Temperature -30.0 °C
 2.38 ft-lb/in²
<br>@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*4; ISO 180/1U
NB
<br>@Temperature -30.0 °C
 NB
<br>@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Taber Abrasion, mg/1000 Cycles 10
10
CS-17, 1 kg; SABIC Method
Optical Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 µm/m-°C
<br>@Temperature 23.0 - 150 °C
 27.8 µin/in-°F
<br>@Temperature 73.4 - 302 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 50.0 µm/m-°C
<br>@Temperature 23.0 - 150 °C
 27.8 µin/in-°F
<br>@Temperature 73.4 - 302 °F
 ISO 11359-2
Thermal Conductivity 0.240 W/m-K
1.67 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 195 °C
383 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 211 °C
412 °F
Rate B/50; ISO 306
212 °C
414 °F
Rate B/120; ISO 306
215 °C
419 °F
Rate A/50; ISO 306
Glass Transition Temp, Tg 217 °C
423 °F
Flammability, UL94 V-0
<br>@Thickness 0.710 mm
 V-0
<br>@Thickness 0.0280 in
 UL 94 by SABIC-IP
5VA
<br>@Thickness 3.00 mm
 5VA
<br>@Thickness 0.118 in
 UL 94 by SABIC-IP
Oxygen Index 44 %
44 %
ISO 4589
Glow Wire Test 960 °C
<br>@Thickness 3.20 mm
 1760 °F
<br>@Thickness 0.126 in
 IEC 60695-2-12
Compliance Properties Metric English Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2
Chemical Resistance Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.9
<br>@Frequency 1.00e+6 Hz
 2.9
<br>@Frequency 1.00e+6 Hz
 IEC 60250
2.9
<br>@Frequency 50.0 - 60.0 Hz
 2.9
<br>@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 28.0 kV/mm
<br>@Thickness 1.60 mm
 711 kV/in
<br>@Thickness 0.0630 in
 in oil; IEC 60243-1
Dissipation Factor 0.00050
<br>@Frequency 50.0 - 60.0 Hz
 0.00050
<br>@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.0025
<br>@Frequency 2.45e+9 Hz
 0.0025
<br>@Frequency 2.45e+9 Hz
 IEC 60250
0.0060
<br>@Frequency 1.00e+6 Hz
 0.0060
<br>@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index >= 100 V
>= 100 V
IEC 60112
150 V
150 V
IEC 60112