Polimeri Europa KOBLEND HI 41 PBT+PC, Impact Grade (discontinued **)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Polimeri Europa KOBLEND HI 41 PBT+PC, Impact Grade
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Symbol according to ISO 1043/1: PBT+PC-HI Elastomer modified PBT+PC blend with very good impact behaviour, ductility even at low temperatures, resistant to solvents, good dimensional stability, good stiffness. Main application fields: automotive industry, structural furnitureUnfilled. Suitable for Injection Molding. Supplied as pellets.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | |
| Melt Flow | 3.5 g/10 min <br>@Load 2.16 kg,<br> Temperature 250 °C |
3.5 g/10 min <br>@Load 4.76 lb,<br> Temperature 482 °F |
cm³/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal |
| Elongation at Yield | 5.5 % | 5.5 % | 50 mm/min |
| Tensile Modulus | 2.00 GPa | 290 ksi | 1 mm/min |
| Izod Impact, Unnotched | NB | NB | |
| NB <br>@Temperature -30.0 °C |
NB <br>@Temperature -22.0 °F |
||
| Izod Impact, Notched (ISO) | 46.0 kJ/m² <br>@Temperature -30.0 °C |
21.9 ft-lb/in² <br>@Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | |
| Vicat Softening Point | 118 °C | 244 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB <br>@Thickness 1.60 mm |
HB <br>@Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 400 V | 400 V |
Users viewing this material also viewed the following:
- Network Polymers NPP 30-2000 TF40
- Eastman M3007-P Polyethylene (discontinued **)
- Lehmann & Voss LUVOCOM® TPE-7829 Thermoplastic elastomer, with PTFE
- Multibase Multi-Flex® A 4541 Clear TPE Thermoplastic Elastomer
- Solvay ALKAMULS® OL 40 Surfactant
- Diamond Polymers Centrex® 925 Injection Molding Grade
- Dow Corning 1664 EMULSION
- AFE Technologies Cronite 34Ni/25Cr/Nb No. HR 33 Nb
- Multibase C6-180 Dow-Corning Class VI Elastomer
Copyright © lookpolymers.com All Rights Reserved