Techmer ES HiFill® PP GB10 10% Glass Beads Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Glass Fiber Filler |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PP GB10 10% Glass Beads Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 10% Filler by WeightInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.970 g/cc | 0.0350 lb/in³ | ASTM D792 |
| Water Absorption | 0.010 % @Time 86400 sec |
0.010 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.023 cm/cm @Thickness 3.17 mm |
0.023 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 92 | 92 | ASTM D785 |
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D638 |
| Elongation at Yield | 10 % | 10 % | ASTM D638 |
| Flexural Yield Strength | 34.5 MPa | 5000 psi | ASTM D790 |
| Flexural Modulus | 1.38 GPa | 200 ksi | ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Thickness 3.17 mm |
0.500 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.4 µm/m-°C | 38.0 µin/in-°F | ASTM D696 |
| Melting Point | 170 °C | 338 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.2 °C | 135 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Nylene® PA6/6 Glass Filled 5133 HS Nylon 6/6
- Huntsman IROGRAN® A 60 E 4902 TPU-Polyester
- Sylvin Technologies 9999-95 Natural PVC Molding Compound
- Teknor Apex APEX® 96-A0914K-106 Polyvinyl Chloride, Flexible
- DuPont Bynel® 42E703 Adhesive Resin
- Chosun Refractories ASM-37 Air-Setting Mortar
- DuPont Teijin Films Melinex® 539 Polyester Film, 370 Gauge
- Techmer ES Plastiblend® ABS 922 NAT
- Radici Radilon® A RV400 (cond.) Nylon 66
Copyright © lookpolymers.com All Rights Reserved