SABIC Innovative Plastics NORYL SE1GFN2 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL SE1GFN2 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE+PS blend. 20% Glass reinforced. Non-brominated, non-chlorinated FR system. UL94 V1 and 5VA listing. RTI 110/105/110. Dielectric strength. Dimensional stability. Suitable for E/E applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 106 | 106 | ASTM D785 |
| Tensile Strength at Break | 106 MPa | 15400 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 151 MPa | 21900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 5.72 GPa | 830 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 1.06 J/cm | 1.99 ft-lb/in | ASTM D256 |
| 0.960 J/cm @Temperature -40.0 °C |
1.80 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 36.0 µm/m-°C @Temperature -40.0 - 95.0 °C |
20.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C @Thickness 6.40 mm |
279 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C @Thickness 6.40 mm |
270 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 110 °C | 230 °F | UL 746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 1.47 mm |
V-1 @Thickness 0.0579 in |
UL 94 |
| V-0 @Thickness 5.99 mm |
V-0 @Thickness 0.236 in |
UL 94 | |
| 5VA @Thickness 2.50 mm |
5VA @Thickness 0.0984 in |
UL 94 | |
| Oxygen Index | 30.9 % | 30.9 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.98 @Frequency 50.0 - 60.0 Hz |
2.98 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| Dielectric Strength | 23.6 kV/mm @Thickness 3.20 mm |
599 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.0016 @Frequency 50.0 - 60.0 Hz |
0.0016 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
| Arc Resistance | 0.00 - 60 sec | 0.00 - 60 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 60 - 120 arcs | 60 - 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- MV Labs FE1060 (NH4)Fe(SO4)2·12H2O Ammonium iron(III) sulfate dodecahydrate
- Raschig Group PiMC 1841 Metallic colors
- Lucite International Diakon® ST25G8 Toughened Acrylic Polymer
- KYDEX® 321 Co-Extruded High Impact Fire Rated Sheet
- SABIC Innovative Plastics LNP LUBRICOMP KP004A Acetal Homopolymer (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP THERMOCOMP RZ006 PA 66
- 3M ATG 928 Tape
- A. Schulman ComAlloy Hiloy® 273 Polystyrene Alloy, Glass Reinforced, Flow Enhanced
- 3M Scotchcal™ 8000-17 Graphic Film
- Kolon SPESIN® KP213G15 Flame Retardant PBT Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved