SABIC Innovative Plastics NORYL PX1007 PPE+HIPS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL PX1007 PPE+HIPS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
NORYL* PX1007 is an unfilled non-chlorinated, non-brominated flame retardant PPE/HIPS grade, targeted for flat panel TV enclosures. It has a Vicat B/120 temperature of 96 degC and UL-94 V0 @ 1.5mm rating.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Moisture Absorption 0.0100 %
0.0100 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.090 %
0.090 %
ISO 62
Melt Index of Compound 10 g/10 min

@Load 1.20 kg,
Temperature 280 °C
 10 g/10 min

@Load 2.65 lb,
Temperature 536 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 41.0 MPa
5950 psi
50 mm/min; ISO 527
Tensile Strength, Yield 53.0 MPa
7690 psi
50 mm/min; ISO 527
Elongation at Break 20 %
20 %
50 mm/min; ISO 527
Elongation at Yield 3.0 %
3.0 %
50 mm/min; ISO 527
Tensile Modulus 2.30 GPa
334 ksi
1 mm/min; ISO 527
Flexural Yield Strength 75.0 MPa
10900 psi
2 mm/min; ISO 178
Flexural Modulus 2.25 GPa
326 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
80*10*4; ISO 180/1A
3.00 kJ/m²

@Temperature -30.0 °C
 1.43 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 50.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 93.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 51.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 74.0 °C
165 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Vicat Softening Point 91.0 °C
196 °F
Rate B/50; ISO 306
96.0 °C
205 °F
Rate B/120; ISO 306
UL RTI, Electrical 95.0 °C
203 °F
UL 746B
UL RTI, Mechanical with Impact 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical without Impact 95.0 °C
203 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 UL 94
5VB

@Thickness 2.50 mm
 5VB

@Thickness 0.0984 in
 UL 94
Oxygen Index 34 %
34 %
ISO 4589
Glow Wire Test 700 °C
1290 °F
IEC 60695-2-13
725 °C
1340 °F
IEC 60695-2-13
725 °C
1340 °F
IEC 60695-2-13
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+16 ohm
>= 1.00e+16 ohm
ROA; IEC 60093
Dielectric Constant 2.8

@Frequency 1.00e+6 Hz
 2.8

@Frequency 1.00e+6 Hz
 IEC 60250
2.9

@Frequency 50.0 - 60.0 Hz
 2.9

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 25.7 kV/mm

@Thickness 1.60 mm
 653 kV/in

@Thickness 0.0630 in
 in oil; IEC 60243-1
Dissipation Factor 0.0041

@Frequency 1.00e+6 Hz
 0.0041

@Frequency 1.00e+6 Hz
 IEC 60250
0.0129

@Frequency 50.0 - 60.0 Hz
 0.0129

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Comparative Tracking Index 400 V
400 V
IEC 60112
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
UL 746A
High Amp Arc Ignition, HAI 30 - 60 arcs
30 - 60 arcs
UL 746A