- Arkema Group VOLTALEF® 300 HD PCTFE
Arkema Group VOLTALEF® 300 HD PCTFE
| Category | Polymer , Thermoplastic , Fluoropolymer , Polychlorotrifluoroethylene (PCTFE); Molded |
| Manufacturer | Arkema |
| Trade Name | VOLTALEF® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group VOLTALEF® 300 HD PCTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
VOLTALEF® 300 HD is a chlorotrifluoroethylene powder. Used for compression molding, very good flow, non-flammable. Information provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.11 - 2.16 g/cc | 0.0762 - 0.0780 lb/in³ | ASTM D1050-68 |
| Apparent Bulk Density | 0.400 - 0.500 g/cc | 0.0145 - 0.0181 lb/in³ | |
| Particle Size | 500 - 600 µm | 500 - 600 µm | |
| Deformation | 1.0 % | 1.0 % | 7 MPa load for 24 hrs at 25°C; ASTM D621 |
| 2.5 % | 2.5 % | 7 MPa load for 24 hrs at 70°C; ASTM D621 | |
| 12 % | 12 % | 7 MPa load for 24 hrs at 125°C; ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 80.0 MPa | 11600 psi | DIN 53456 |
| Hardness, Shore D | 75 - 90 | 75 - 90 | ASTM D676 |
| Tensile Strength, Ultimate | 32.0 - 40.0 MPa | 4640 - 5800 psi | ASTM D638 |
| 13.0 - 16.0 MPa @Temperature 120 °C |
1890 - 2320 psi @Temperature 248 °F |
ASTM D638 | |
| Tensile Strength, Yield | 34.0 - 50.0 MPa | 4930 - 7250 psi | ASTM D638 |
| 3.00 - 6.00 MPa @Temperature 120 °C |
435 - 870 psi @Temperature 248 °F |
ASTM D638 | |
| Elongation at Break | 100 - 250 % | 100 - 250 % | ASTM D638 |
| Tensile Modulus | 1.40 GPa | 203 ksi | ASTM D638 |
| Flexural Modulus | 1.40 GPa | 203 ksi | ASTM D790-80 |
| Compressive Yield Strength | 11.0 - 14.0 MPa | 1600 - 2030 psi | 1% deformation; ISO 604 |
| 40.0 - 45.0 MPa | 5800 - 6530 psi | 0.2% off set; ISO 604 | |
| Compressive Modulus | 1.40 GPa | 203 ksi | ASTM D638 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256-81 |
| Coefficient of Friction | 0.26 - 0.45 | 0.26 - 0.45 | on polished steel |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 55.0 µm/m-°C @Temperature -80.0 - 70.0 °C |
30.6 µin/in-°F @Temperature -112 - 158 °F |
ASTM D686-79 |
| 250 µm/m-°C @Temperature 70.0 - 150 °C |
139 µin/in-°F @Temperature 158 - 302 °F |
ASTM D686-79 | |
| Specific Heat Capacity | 0.900 J/g-°C | 0.215 BTU/lb-°F | |
| Thermal Conductivity | 0.135 W/m-K | 0.937 BTU-in/hr-ft²-°F | F 433 |
| Maximum Service Temperature, Air | 150 °C | 302 °F | continuous service |
| 200 °C | 392 °F | peak | |
| Oxygen Index | 100 % | 100 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.20e+18 ohm-cm | 1.20e+18 ohm-cm | ASTM D257-78 |
| Dielectric Constant | 2.4 - 3.0 @Frequency 100 - 1.00e+8 Hz |
2.4 - 3.0 @Frequency 100 - 1.00e+8 Hz |
ASTM D150 |
| Dielectric Strength | 15.0 kV/mm @Thickness 3.20 mm |
381 kV/in @Thickness 0.126 in |
stepwise tension increase; ASTM D149-75 |
| 21.0 kV/mm @Thickness 1.60 mm |
533 kV/in @Thickness 0.0630 in |
continuous tension; ASTM D149-75 | |
| 48.0 kV/mm @Thickness 0.760 mm |
1220 kV/in @Thickness 0.0299 in |
stepwise tension increase; ASTM D149-75 | |
| 200 kV/mm @Thickness 0.130 mm |
5080 kV/in @Thickness 0.00512 in |
stepwise tension increase; ASTM D149-75 | |
| Arc Resistance | 360 sec | 360 sec | ASTM D495-73 |
Users viewing this material also viewed the following:
- MarkeTech Resorcinol Formaldehyde Aerogel
- LG Chemical Lupox® LW5300M PBT+PC+MF30%
- Indium Corp. In(NO3)3 x 4.5H2O Hydrated Indium Nitrate
- Struktol TPW 709 Processing Additive
- SABIC Innovative Plastics Valox® SLWM2105 PBT+PC (Asia Pacific)
- Total PSI 945 Polystyrene
- Tra-Con Tra-Coat WCC2A Clear Dual-Cure Semi-Flexible Adhesive
- Dow Corning 7-9245 30% SIMETHICONE EMULSION USP
- Domo Domamid® 24 Polyamide 6
- ArcelorMittal Dual Phase 980 Y700 Very high strength steel, Cold Rolled Steel
Copyright © lookpolymers.com All Rights Reserved