Borealis HF136MO Polypropylene

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Borealis
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Borealis HF136MO Polypropylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

HF136MO is a polypropylene homopolymer intended for injection molding. This grade is characterized by a good combination of mechanical and flow properties. This polymer is a CR (controlled rheology) grade with narrow molecular weight distribution giving low warpage. Applications: caps and closuresInformation provided by Borealis AG

Physical Properties	Metric	English	Comments
Density	0.908 g/cc	0.0328 lb/in³	ISO 1183
Linear Mold Shrinkage	0.010 - 0.020 cm/cm	0.010 - 0.020 in/in
Melt Flow	20 g/10 min @Load 2.16 kg, Temperature 230 °C	20 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	98	98	ISO 2039-2
Tensile Strength, Yield	34.0 MPa	4930 psi	50mm/min; ISO 527-2
Elongation at Yield	9.0 %	9.0 %	50mm/min; ISO 527-2
Tensile Modulus	1.50 GPa	218 ksi	1mm/min; ISO 527-2
Charpy Impact, Notched	0.350 J/cm² @Temperature 23.0 °C	1.67 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	92.0 °C	198 °F	ISO 75-2

Processing Properties	Metric	English
Melt Temperature	230 - 260 °C	446 - 500 °F
Mold Temperature	10.0 - 30.0 °C	50.0 - 86.0 °F
Hold Pressure	20.0 - 50.0 MPa	2900 - 7250 psi

Descriptive Properties	Value	Comments
Injection Velocity	highest possible