SABIC Innovative Plastics NORYL GTX GTX985 PPE+PA66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Polyphenylene Ether/PPO |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX985 PPE+PA66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
NORYL GTX985 is a 18% mineral filled material. This material combines high stiffness and excellent temperature resistance with conductivity for electrostatic painting.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.10 % | 1.10 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm @Thickness 3.20 mm |
0.011 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 16 g/10 min @Load 5.00 kg, Temperature 280 °C |
16 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 15 g/10 min @Load 5.00 kg, Temperature 280 °C |
15 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | Type I, 5 mm/min; ASTM D638 |
| 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | Type I, 5 mm/min; ASTM D638 |
| 65.0 MPa | 9430 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 |
| 7.0 % | 7.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D638 |
| 4.0 % | 4.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.40 GPa | 638 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 105 MPa | 15200 psi | 2 mm/min; ISO 178 |
| 110 MPa | 16000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 4.20 GPa | 609 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.35 GPa | 631 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in | ASTM D256 |
| 0.400 J/cm @Temperature -30.0 °C |
0.749 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | 80*10*3; ISO 180/1U |
| 55.0 kJ/m² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 60.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
33.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 65.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
36.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 200 °C @Thickness 3.20 mm |
392 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 195 °C | 383 °F | Rate B/50; ASTM D1525 |
| 195 °C | 383 °F | Rate B/50; ISO 306 | |
| 200 °C | 392 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Heatbath/Park High Temp Draw Salt Quenching and Tempering Salt
- Taiwan Sheen Soon Sheenthane® AS-120H TPU for PU Adhesive
- Sharadaa Ceramics PCF70 (M) Precast Prefired Brick
- Sawbones Cellular Rigid Polyurethane Foam 20 pcf Density
- A. Schulman FORMION™ FI 401 Ionomer
- Fainplast Compounds CKL 8318/2 Flexible PVC, Sheathing Lead Free
- ChevronTexaco Delo® 1000 Marine Engine Oil, SAE 50
- Chang Chun Plastic Longlite PM T310 Impact Phenolic Molding Compound
- Aremco Ceramabind™ 642-A High Temperature Inorganic Binder
- Braskem EB 861/51 LDPE Blown Film Extrusion Polyethylene
Copyright © lookpolymers.com All Rights Reserved