Sharadaa Ceramics THERMO PATCH EXCEL High Alumina Castables
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Sharadaa Ceramics |
| Trade Name | THERMO |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sharadaa Ceramics THERMO PATCH EXCEL High Alumina Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: We bring to our clients a qualitative range of Dense Alumina Castables that are conventional castable of medium purity. These castables cater to the application needs of various industries such as steel, cement, petrochemical and non-ferrous industries.Information provided by Sharadaa Ceramics Pvt. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | >= 2.75 g/cc | >= 0.0994 lb/in³ | Dried at 110°C |
| Grain Size | <= 5000 µm | <= 5000 µm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.00735 GPa @Temperature 1100 °C |
1.07 ksi @Temperature 2010 °F |
|
| 0.0118 GPa @Temperature 110 °C |
1.71 ksi @Temperature 230 °F |
||
| 0.0127 GPa @Temperature 1500 °C |
1.84 ksi @Temperature 2730 °F |
||
| Compressive Strength | 58.8 MPa @Temperature 1100 °C |
8530 psi @Temperature 2010 °F |
Cold Crushing |
| 68.6 MPa @Temperature 1500 °C |
9960 psi @Temperature 2730 °F |
Cold Crushing | |
| 93.2 MPa @Temperature 110 °C |
13500 psi @Temperature 230 °F |
Cold Crushing | |
| 34.3 MPa @Time 86400 sec |
4980 psi @Time 24.0 hour |
Cold Crushing |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 1.34 W/m-K @Temperature 400 °C, Time 10800 sec |
9.30 BTU-in/hr-ft²-°F @Temperature 752 °F, Time 3.00 hour |
|
| 1.42 W/m-K @Temperature 600 °C, Time 10800 sec |
9.85 BTU-in/hr-ft²-°F @Temperature 1110 °F, Time 3.00 hour |
||
| 1.53 W/m-K @Temperature 800 °C, Time 10800 sec |
10.6 BTU-in/hr-ft²-°F @Temperature 1470 °F, Time 3.00 hour |
||
| Maximum Service Temperature, Air | 1600 °C | 2910 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Fe2O3 | <= 0.70 % | <= 0.70 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Permanent Linear Change | <-0.05 | 800°C |
| <-0.12 | 1100°C | |
| <-0.6 | 1500°C | |
| Refractoriness | <1750°C | |
| Thermal Expansion | 0.8 | Reversible |
| Water Required to Mix | 10-12% |
Users viewing this material also viewed the following:
- Arlon 31580R015 0.015" (0.381 mm) Uncured Unsupported Silicone Rubber on an HDPE Carrier (discontinued *
- LyondellBasell Lupolen® 2425 K LDPE, Film Grade
- Ferro IP 530 Thick Film Glass
- Teknor Apex Sarlink® 4190 Thermoplastic Elastomer
- A. Schulman POLYBATCH™ CE-505-E Concentrate Based In Polyethylene
- A. Schulman POLYBATCH™ White LL8970 TS Concentrate Based In LLDPE
- Hexcel® HexPly® EH04 Epoxy Resin System, Fortafil 510 Fiber
- Arkema Group KYNAR® 740 Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion
- ExxonMobil Label-Lyte® 612 LL-112 Clear OPP Overlaminate
- Borealis Bormod™ HF955MO Polypropylene Homopolymer for Injection Molding
Copyright © lookpolymers.com All Rights Reserved