SABIC Innovative Plastics NORYL GFN1720 PPE+HIPS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GFN1720 PPE+HIPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl* GFN1720 is a 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Noryl GFN1720 is available in multiple colors and may be an excellent material candidate for ignition coils, bobbins and other application requiring electrically insulating properties.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.15 % | 0.15 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | on Tensile Bar; SABIC Method |
| 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method | |
| Melt Flow | 4.5 g/10 min @Load 5.00 kg, Temperature 300 °C |
4.5 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 11 g/10 min @Load 10.0 kg, Temperature 300 °C |
11 g/10 min @Load 22.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 100 MPa | 14500 psi | ISO 2039-1 |
| Tensile Strength at Break | 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 |
| 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 |
| 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 5.50 GPa | 798 ksi | 5 mm/min; ASTM D638 |
| 6.00 GPa | 870 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 135 MPa | 19600 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 145 MPa | 21000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.50 GPa | 653 ksi | 2 mm/min; ISO 178 |
| 4.80 GPa | 696 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256 |
| 0.500 J/cm @Temperature -30.0 °C |
0.937 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| 25.0 kJ/m² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 2.50 J/cm² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Dart Drop, Total Energy | 14.0 J @Temperature 23.0 °C |
10.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Taber Abrasion, mg/1000 Cycles | 45 | 45 | CS-17, 1 kg; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
16.7 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| 40.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
22.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 70.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Thermal Conductivity | 0.260 W/m-K | 1.80 BTU-in/hr-ft²-°F | ISO 8302 |
| Hot Ball Pressure Test | <= 165 °C | <= 329 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 171 °C @Thickness 3.20 mm |
340 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 170 °C | 338 °F | Rate B/50; ISO 306 |
| 180 °C | 356 °F | Rate B/120; ISO 306 | |
| 180 °C | 356 °F | Rate A/50; ISO 306 | |
| 181 °C | 358 °F | Rate B/50; ASTM D1525 | |
| UL RTI, Electrical | 65.0 °C | 149 °F | UL 746B |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | UL 746B |
| UL RTI, Mechanical without Impact | 65.0 °C | 149 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
UL 94 | |
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Glow Wire Test | 960 °C @Thickness 3.20 mm |
1760 °F @Thickness 0.126 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.6 @Frequency 1.00e+6 Hz |
2.6 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.7 @Frequency 50.0 - 60.0 Hz |
2.7 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 16.0 kV/mm @Thickness 3.20 mm |
406 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| 26.0 kV/mm @Thickness 1.60 mm |
660 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| 30.0 kV/mm @Thickness 0.800 mm |
762 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |
| Dissipation Factor | 0.0020 @Frequency 1.00e+6 Hz |
0.0020 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.0060 @Frequency 50.0 - 60.0 Hz |
0.0060 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Polimeri Europa Sinkral® C 442 ABS Resin
- LG Chemical Lupox® GP2306FG PBT+GF30%
- Styrolution Terluran® GP-25 ABS
- A. Schulman SCHULAMID® 6 GF15H 15% Glass Fiber Reinforced, Heat Impact Nylon 6
- A. Schulman POLYFORT™ FPP 1606 Glass Filled Chemically Coupled Impact Copolymer Polypropylene
- DuPont Vamac® DP Test Compound
- A. Schulman LP481 Molding Grade High-Density Polyethylene
- Daikin NEOFLON AP-201SH PFA Semiconductor Grade
- Chi Mei Kibiton® PB-5903 SBC
- Borealis Daplen™ PB4432 TPO Compound
Copyright © lookpolymers.com All Rights Reserved