Techmer ES Electrablend® PC/PET CF20 IM 20% Carbon Filled
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Conductive , Polycarbonate/PET Polyester Blend, Carbon Fiber Filled , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | Techmer ES |
| Trade Name | Electrablend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Electrablend® PC/PET CF20 IM 20% Carbon Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber Reinforcement, 20% Filler by WeightAdditive: Impact ModifierFeatures: Impact Modified and Semi ConductiveAppearance: BlackInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ASTM D792 |
| Water Absorption | 0.080 % @Time 86400 sec |
0.080 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 3.17 mm |
0.0060 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Yield | 124 MPa | 18000 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Yield Strength | 179 MPa | 26000 psi | ASTM D790 |
| Flexural Modulus | 9.31 GPa | 1350 ksi | ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm @Thickness 3.17 mm |
1.80 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 3.20 J/cm @Thickness 3.17 mm |
6.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.8 µm/m-°C | 11.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0590 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+7 ohm-cm | 1.00e+7 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+7 ohm | 1.00e+7 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PE 4020W (20425) Linear Low Density Polyethylene
- PTS Tristar® PC-10R-CL(V6) 6 MFI UV Stabilized Clear Polycarbonate with Release
- PlastiComp Complet® LCF40 - PA66 MT Nylon 66, 40% Long Carbon Fiber Reinforced, Impact Modified
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, Hardness 52A
- Spartech Polypedic F High Density Polyethylene
- Silberline Sparkle Silvet® Premier 838-30-E1
- A. Schulman POLYBATCH™ Blue LL40348/4 Concentrate Based In LLDPE
- BASF Elastollan® S95A Polyester Type Polyurethane Elastomer
Copyright © lookpolymers.com All Rights Reserved