SABIC Innovative Plastics NORYL FXN121LG PPE+HIPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL FXN121LG PPE+HIPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl* FXN121LG is an unfilled modified polyphenylene ether resin suitable for injection molding. Designed to possess a unique low gloss surface appearance even when molded in polished tools, this resin uses non-chlorinated, non-brominated FR additives to achieve a V1 UL94 rating. FXN121LG is available multiple colors and may be an excellent choice for a wide variety of applications including hand held devises, housings and displays.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.23 % | 0.23 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 12 g/10 min @Load 5.00 kg, Temperature 280 °C |
12 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 12 g/10 min @Load 5.00 kg, Temperature 280 °C |
12 g/10 min @Load 11.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ISO 2039-2 |
| Hardness, H358/30 | 105 MPa | 15200 psi | ISO 2039-1 |
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 |
| 53.0 MPa | 7690 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 30 % | 30 % | 50 mm/min; ISO 527 |
| 30 % | 30 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 4.6 % | 4.6 % | 50 mm/min; ISO 527 |
| 4.8 % | 4.8 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.30 GPa | 334 ksi | 5 mm/min; ASTM D638 |
| 2.35 GPa | 341 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
| 97.0 MPa | 14100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| 2.40 GPa | 348 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.20 J/cm | 2.25 ft-lb/in | ASTM D256 |
| 0.700 J/cm @Temperature -30.0 °C |
1.31 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 41.0 J @Temperature 23.0 °C |
30.2 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Taber Abrasion, mg/1000 Cycles | 60 | 60 | CS-17, 1 kg; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 82.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 82.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 85.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 85.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 130 °C @Thickness 3.20 mm |
266 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 116 °C @Thickness 3.20 mm |
241 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 135 °C | 275 °F | Rate B/50; ISO 306 |
| 137 °C | 279 °F | Rate B/50; ASTM D1525 | |
| 138 °C | 280 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
UL 94 |
| Oxygen Index | 30 % | 30 % | ISO 4589 |
| Glow Wire Test | 700 °C | 1290 °F | IEC 60695-2-13 |
| 960 °C @Thickness 3.20 mm |
1760 °F @Thickness 0.126 in |
IEC 60695-2-12 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 20 % | 20 % | untextured, 60 degrees; ASTM D523 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.7 @Frequency 1.00e+6 Hz |
2.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.7 @Frequency 50.0 - 60.0 Hz |
2.7 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 16.0 kV/mm @Thickness 3.20 mm |
406 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0020 @Frequency 1.00e+6 Hz |
0.0020 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.0040 @Frequency 50.0 - 60.0 Hz |
0.0040 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | Passes | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- LyondellBasell Plexar® PX2049 Extrudable Tie-Layer Resin - Anhydride Modified HDPE (discontinued **)
- SGL Carbon Group SIGRAFIL C® C25 S003 EPY Staple Carbon Fiber, Epoxy Sizing
- DSM Novamid® ST220 NAT PA6-I
- ExxonMobil Metallyte™ 38MW480 OPP Film
- BASF Ultramid® 8270 HS PA6 (Dry)
- 3M 7690-S Cold Shrink QT-III Silicone Rubber Skirted Termination Kits
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 0.0 PHR Zinc Stearate
- Pau Tai UNISTAB BZ-591 Liquid Barium-Zinc Stabilizer
- Ineos Nova 4210 Medium Impact Polystyrene (discontinued **)
- SABIC Innovative Plastics NORYL EM6100 PPE+PS (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved