Polyram PlusTek RB506 Nylon 6, Flame Retardant
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek RB506 Nylon 6, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | DIN 53479 |
| Linear Mold Shrinkage | 0.014 - 0.016 cm/cm | 0.014 - 0.016 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | >= 60.0 MPa | >= 8700 psi | ASTM-D638 |
| Elongation at Break | >= 15 % | >= 15 % | ASTM-D638 |
| Flexural Strength | >= 90.0 MPa | >= 13100 psi | ASTM D790 |
| Flexural Modulus | >= 2.20 GPa | >= 319 ksi | ASTM-D790 |
| Izod Impact, Notched | >= 0.400 J/cm @Temperature 23.0 °C |
>= 0.749 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 218 °C | 424 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 150 °C | >= 302 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 70.0 °C | >= 158 °F | DIN 53461 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
Users viewing this material also viewed the following:
- Outokumpu 4567 Austenitic Stainless Steel
- Permabond TA4300 Toughened Acrylic Adhesive
- Lehmann & Voss LUVOCOM® 1105-8059 PEEK, lubricant modified, easy flowing
- Lucent Polymers CPP-230 Polypropylene, 30% Calcium Carbonate Filled, Impact Modified
- Teknor Apex APEX® 80855 Polyvinyl Chloride, Flexible
- Zircar Zirconia HfF-100 Hafnia Felt Insulation
- ExxonMobil PP7033N Impact Copolymer
- Aremco Aremco-Seal™ 529VHV High Temperature Specialty Coatings Silicone
- Teijin Panlite® BN-8120R Improved Mold Release, Carbon Fiber Reinforced, Flame Resistant Polycarbonate Resin
- Lehmann & Voss LUVOCOM® 1-7497 Polyamide 66, with PTFE, lubricant modified, heat stabilized
Copyright © lookpolymers.com All Rights Reserved