SABIC Innovative Plastics NORYL 731 PPE+HIPS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL 731 PPE+HIPS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PPE+PS, HDT 125
Physical Properties Metric English Comments
Specific Gravity 1.08 g/cc
1.08 g/cc
ASTM D792
Water Absorption 0.13 %

@Time 86400 sec
 0.13 %

@Time 24.0 hour
 ISO 62-1
Moisture Absorption 0.0400 %
0.0400 %
50% RH, 24 hrs; ISO 62-4
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 11 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 11 g/10 min

@Load 11.0 lb,
Temperature 536 °F
 ASTM D1238
Melt Index of Compound 12 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 12 g/10 min

@Load 11.0 lb,
Temperature 536 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
50 mm/min; ISO 527
45.0 MPa
6530 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 40.0 MPa
5800 psi
50 mm/min; ISO 527
54.0 MPa
7830 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 30 %
30 %
Type I, 50 mm/min; ASTM D638
70 %
70 %
50 mm/min; ISO 527
Elongation at Yield 4.0 %
4.0 %
Type I, 50 mm/min; ASTM D638
70 %
70 %
50 mm/min; ISO 527
Tensile Modulus 2.10 GPa
305 ksi
1 mm/min; ISO 527
2.40 GPa
348 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 75.0 MPa
10900 psi
1.3 mm/min, 50 mm span; ASTM D790
80.0 MPa
11600 psi
2 mm/min; ISO 178
Flexural Modulus 2.10 GPa
305 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.30 GPa
334 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.50 J/cm
2.81 ft-lb/in
ASTM D256
1.20 J/cm

@Temperature -30.0 °C
 2.25 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Unnotched 8.00 J/cm
15.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 16.0 kJ/m²
7.61 ft-lb/in²
80*10*4; ISO 180/1A
11.0 kJ/m²

@Temperature -30.0 °C
 5.23 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 60.0 kJ/m²
28.6 ft-lb/in²
80*10*4; ISO 180/1U
55.0 kJ/m²

@Temperature -30.0 °C
 26.2 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact, Notched 1.30 J/cm²
6.19 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 55.0 J

@Temperature 23.0 °C
 40.6 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 40.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
73.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 40.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 44.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
83.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 46.1 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 112 °C
234 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
110 °C

@Thickness 3.20 mm
 230 °F

@Thickness 0.126 in
 unannealed; ASTM D648
124 °C

@Thickness 6.40 mm
 255 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 133 °C
271 °F
Rate B/50; ASTM D1525
133 °C
271 °F
Rate B/50; ISO 306
135 °C
275 °F
Rate B/120; ISO 306