SABIC Innovative Plastics Lexan® HPX8R PC Copolymer (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® HPX8R PC Copolymer (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Very high flow specialty polycarbonate with outstanding processability and ductility. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). ETO sterilizable. Contains mold release.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0900 % | 0.0900 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.12 % | 0.12 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 35 g/10 min @Load 1.20 kg, Temperature 300 °C |
35 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 33 g/10 min @Load 1.20 kg, Temperature 300 °C |
33 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 90 | 90 | ASTM D785 |
| Tensile Strength at Break | 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 |
| 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 59.0 MPa | 8560 psi | Type I, 50 mm/min; ASTM D638 |
| 59.0 MPa | 8560 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 118.6 % | 118.6 % | 50 mm/min; ISO 527 |
| 118.9 % | 118.9 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 5.4 % | 5.4 % | 50 mm/min; ISO 527 |
| 5.7 % | 5.7 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.36 GPa | 342 ksi | 50 mm/min; ASTM D638 |
| 2.40 GPa | 348 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
| 99.0 MPa | 14400 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.25 GPa | 326 ksi | 2 mm/min; ISO 178 |
| 2.35 GPa | 341 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 7.02 J/cm | 13.2 ft-lb/in | ASTM D256 |
| 2.20 J/cm @Temperature -30.0 °C |
4.12 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 60.0 kJ/m² | 28.6 ft-lb/in² | 80*10*3; ISO 180/1A |
| 30.0 kJ/m² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 6.00 J/cm² | 28.6 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 79.0 J @Temperature 23.0 °C |
58.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 65.0 µm/m-°C @Temperature -40.0 - 95.0 °C |
36.1 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| 65.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
36.1 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 74.0 µm/m-°C @Temperature -40.0 - 95.0 °C |
41.1 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| 74.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
41.1 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 117 °C | 243 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 120 °C @Thickness 3.20 mm |
248 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 137 °C | 279 °F | Rate B/50; ISO 306 |
| 138 °C | 280 °F | Rate A/50; ASTM D1525 | |
| 140 °C | 284 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 130 °C | 266 °F | UL 746B |
| UL RTI, Mechanical without Impact | 130 °C | 266 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
| Glow Wire Test | 825 °C | 1520 °F | IEC 60695-2-13 |
| 850 °C | 1560 °F | IEC 60695-2-13 | |
| 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
IEC 60695-2-12 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 3.0 % @Thickness 2.54 mm |
3.0 % @Thickness 0.100 in |
ASTM D1003 |
| Transmission, Visible | 82 % | 82 % | 2.54 mm; ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ASTM D257 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASS | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers GTPR-1358A
- Precision Polymer Engineering S60E Silicone Rubber
- SABIC Innovative Plastics LNP KONDUIT OTF2B PPS - Linear
- Silberline Extra Fine "A"
- Teknor Apex APEX® 3610-70 Polyvinyl Chloride, Flexible
- Ecomass® 1850ZC84 Stainless Steel Powder Filled Polyamide (PA6), Injection Molding
- Ashley Polymers Ashlene® P1044R Polycarbonate
Copyright © lookpolymers.com All Rights Reserved