SABIC Innovative Plastics Lexan® HFD4211 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® HFD4211 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lexan* HFD4211 is a 10% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.120 % | 0.120 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.30 % | 0.30 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 18 g/10 min @Load 1.20 kg, Temperature 300 °C |
18 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
12 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 5 mm/min; ASTM D638 |
| 59.0 MPa | 8560 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | Type I, 5 mm/min; ASTM D638 |
| 68.0 MPa | 9860 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.2 % | 3.2 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 2.7 % | 2.7 % | 5 mm/min; ISO 527 |
| 3.1 % | 3.1 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 4.12 GPa | 598 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 102 MPa | 14800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 3.69 GPa | 535 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 1.20 J/cm | 2.25 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 12.6 J/cm | 23.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*3; ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 64.0 kJ/m² | 30.5 ft-lb/in² | 80*10*3; ISO 180/1U |
| 60.0 kJ/m² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | 7.50 J/cm² | 35.7 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| 8.10 J/cm² @Temperature -30.0 °C |
38.5 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 50.0 J @Temperature 23.0 °C |
36.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
22.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 40.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
22.2 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 80.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C @Thickness 3.20 mm |
264 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 141 °C | 286 °F | Rate B/120; ISO 306 |
| UL RTI, Electrical | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 0.300 mm |
HB @Thickness 0.0118 in |
UL 94 |
| Glow Wire Test | 850 °C | 1560 °F | IEC 60695-2-13 |
| 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
IEC 60695-2-12 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Nye Lubricants 825-1 (FG) Synthetic Oil
- Iran Petrochemical (PCC) LS0085 Low Density Polyethylene
- Kraton® D1155 B (SBS) Liner Block Copolymer
- Lanxess Durethan® AC 30 000000 Nylon 66
- Gwent Electronic Materials P2121112P4 Nitrogen Plasma Modified Graphene Nanoplatelets
- Polyram RamOfin PPC501 Polypropylene, Flame Retardant
- A. Schulman POLYBLAK™ 3422 Black Color Concentrate, 35% Carbon Black Based In LDPE
- Aclo Accutech Polypropylene Homopolymer HP0339W30L1 Wollastonite Reinforced
- BP Amoco Accpro® 9346 Enhanced Polypropylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved