SABIC Innovative Plastics Lexan® HF1110R PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® HF1110R PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow grade. Easy mold release version of LEXAN HF1110. For thin wall lighting lenses, data storage components and safety eyewear lenses.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 25 g/10 min @Load 1.20 kg, Temperature 300 °C |
25 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 120 % | 120 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 6.40 J/cm | 12.0 ft-lb/in | ASTM D256 |
| Tensile Impact Strength | 378 kJ/m² | 180 ft-lb/in² | Type S; ASTM D1822 |
| Dart Drop, Total Energy | 54.0 J | 39.8 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C @Thickness 3.20 mm |
259 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 130 °C | 266 °F | UL 746B |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | UL 746B |
| UL RTI, Mechanical without Impact | 130 °C | 266 °F | UL 746B |
| Flammability, UL94 | V-2 @Thickness 1.09 mm |
V-2 @Thickness 0.0429 in |
UL 94 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.0 % @Thickness 2.54 mm |
1.0 % @Thickness 0.100 in |
ASTM D1003 |
| Transmission, Visible | 88 % | 88 % | 2.54 mm; ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | UL 746A |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
| High Amp Arc Ignition, HAI | 60 - 120 arcs | 60 - 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PH 63 T 20 PP, 20% mineral filling
- LG Chemical LUMID GN-2251BF Flame Retardant PA Alloy
- Minelco MicroSpar
- Techmer ES HiFill® PA6/6 GF33 LE 33% Glass Filled
- A. Schulman SCHULAFLEX® SF 302 Ethylene-Based Butene Plastomer
- CP-Polymer-Technik Wellamid® 6600/506 HWCP Nylon 66, Impact Modified, Heat Stabilized, Dry
- A. Schulman ComAlloy Lubrilon® 62S1 Internally Lubricated, Nylon 6/6
- 3M Scotchcal™ 3475 Graphic Film
- GEHR Plastics ECOGEHR® PA 11 Nylon 11 Dry (discontinued **)
Copyright © lookpolymers.com All Rights Reserved