E-Polymers TEKAMID® TB110SG30 30% Glass Fiber Reinforced, High Impact PA6 Resin

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer	E-Polymers Co. Ltd.
Trade Name	TEKAMID®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	E-Polymers TEKAMID® TB110SG30 30% Glass Fiber Reinforced, High Impact PA6 Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polyamide (Nylon) Resin. TEKAMID is widely being used in manufacturing of automotive and industrial parts with its outstanding mechanical, thermal and chemical properties.T-series: Impact modified, Super tough productsInformation Provided by E-Polymers Co., Ltd.

Physical Properties	Metric	English	Comments
Specific Gravity	1.34 g/cc	1.34 g/cc	ASTM D792
Water Absorption	0.90 % @Time 86400 sec	0.90 % @Time 24.0 hour
Linear Mold Shrinkage	0.0030 cm/cm	0.0030 in/in
Linear Mold Shrinkage, Transverse	0.0080 cm/cm	0.0080 in/in

Mechanical Properties	Metric	English	Comments
Tensile Strength	142 MPa	20600 psi	ASTM D638
Elongation at Break	3.5 %	3.5 %	ASTM D638
Flexural Strength	186 MPa	27000 psi	ASTM D790
Flexural Modulus	6.08 GPa	882 ksi	ASTM D790
Izod Impact, Notched	2.35 J/cm	4.41 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	ASTM D2133
Deflection Temperature at 0.46 MPa (66 psi)	210 °C	410 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	200 °C	392 °F	ASTM D648
Flammability, UL94	HB	HB

Processing Properties	Metric	English	Comments
Melt Temperature	270 - 290 °C	518 - 554 °F
Mold Temperature	80.0 - 90.0 °C	176 - 194 °F