SABIC Innovative Plastics Lexan® FXD1413T PC Copolymer (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® FXD1413T PC Copolymer (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Clear PC-siloxane copolymer with excellent processability, in special light diffusion colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D 792 |
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.090 % | 0.090 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.13 % @Temperature 23.0 °C |
0.13 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | on tensile bar; SABIC Method |
| 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 9.0 g/10 min @Load 5.00 kg, Temperature 220 °C |
9.0 g/10 min @Load 11.0 lb, Temperature 428 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 50 mm/min; ISO 527 |
| 66.0 MPa | 9570 psi | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | 50 mm/min; ISO 527 |
| 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Break | 116 % | 116 % | 50 mm/min; ISO 527 |
| 130 % | 130 % | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Yield | 5.6 % | 5.6 % | 50 mm/min; ISO 527 |
| 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Modulus | 2.27 GPa | 329 ksi | 50 mm/min; ASTM D 638 |
| 2.31 GPa | 335 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 87.0 MPa | 12600 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 91.0 MPa | 13200 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 2.19 GPa | 318 ksi | 2 mm/min; ISO 178 |
| 2.27 GPa | 329 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 7.95 J/cm @Temperature -30.0 °C |
14.9 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 8.90 J/cm @Temperature 23.0 °C |
16.7 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 55.0 kJ/m² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A |
| 65.0 kJ/m² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Impact Test | 82.0 J @Temperature 23.0 °C |
60.5 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 71.5 µm/m-°C @Temperature 23.0 - 80.0 °C |
39.7 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| 71.5 µm/m-°C @Temperature -40.0 - 95.0 °C |
39.7 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 79.3 µm/m-°C @Temperature 23.0 - 80.0 °C |
44.1 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| 79.3 µm/m-°C @Temperature -40.0 - 95.0 °C |
44.1 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 119 °C | 246 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 141 °C | 286 °F | Rate A/50; ASTM D 1525 |
| 141 °C | 286 °F | Rate B/50; ISO 306 | |
| 143 °C | 289 °F | Rate B/120; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASS | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- ExxonMobil Vyram™ 9101-45 Thermoplastic Elastomer (discontinued **)
- Ravago Manufacturing Americas Hylon® N1000STHLUV2 HF Nylon 6/6 (discontinued **)
- Huntsman Araldite PZ 3902 Water-Based Adhesive/Coating
- Samsung Cheil Industries Starex® BF-0930 MABS, Unreinforced Scratch Resistant
- A. Schulman SCHULADUR® A GF30 30% Glass Fiber Reinforced PBT
- DSM Akulon® F223-D (Cond.) Low/Medium Viscosity Nylon 6 (North America)
- ExxonMobil 825 Mobil SHC 800 Series
- California Fine Wire Nickel 272 Super Alloy
- Arkema Group Evatane® 1005 VN 4 Ethylene Vinyl Acetate
Copyright © lookpolymers.com All Rights Reserved