SABIC Innovative Plastics Lexan® CFR5630 PC COPOLYMER (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® CFR5630 PC COPOLYMER (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LEXAN™ CFR5630 Polycarbonate (PC) is a non-filled resin, suitable for injection molding and extrusion. This non-chlorinated, non-brominated flame retardant PC resin meets FAR25.853 smoke density and 60 second vertical burn and OEM toxicity requirements. LEXAN CFR5630 resin is available in transparent and opaque colors.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption 0.110 %
0.110 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.14 %
0.14 %
ISO 62
Linear Mold Shrinkage, Flow 0.0055 - 0.0075 cm/cm

@Thickness 3.20 mm
0.0055 - 0.0075 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 5.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
5.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 5.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
5.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 52.0 MPa
7540 psi
Type I, 50 mm/min; ASTM D638
52.0 MPa
7540 psi
50 mm/min; ISO 527
Tensile Strength, Yield 67.0 MPa
9720 psi
50 mm/min; ISO 527
68.0 MPa
9860 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 23 %
23 %
50 mm/min; ISO 527
51 %
51 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 6.0 %
6.0 %
Type I, 50 mm/min; ASTM D638
6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 2.40 GPa
348 ksi
1 mm/min; ISO 527
2.50 GPa
363 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 103 MPa
14900 psi
2 mm/min; ISO 178
106 MPa
15400 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.40 GPa
348 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.50 GPa
363 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.00 J/cm
1.87 ft-lb/in
ASTM D256
0.850 J/cm

@Temperature -30.0 °C
1.59 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched 21.5 J/cm
40.3 ft-lb/in
ASTM D4812
20.0 J/cm

@Temperature -30.0 °C
37.5 ft-lb/in

@Temperature -22.0 °F
ASTM D4812
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*3; ISO 180/1A
9.00 kJ/m²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched 13.2 J/cm²
62.8 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eU
12.9 J/cm²

@Temperature -30.0 °C
61.4 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
0.900 J/cm²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 66.0 J

@Temperature 23.0 °C
48.7 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 66.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
36.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
72.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
40.0 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
76.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
42.2 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 131 °C
268 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
131 °C

@Thickness 3.20 mm
268 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
120 °C

@Thickness 3.20 mm
248 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 136 °C
277 °F
Rate B/50; ASTM D1525
137 °C
279 °F
Rate B/50; ISO 306
139 °C
282 °F
Rate B/120; ISO 306
UL RTI, Electrical 125 °C
257 °F
UL 746B
UL RTI, Mechanical with Impact 120 °C
248 °F
UL 746B
UL RTI, Mechanical without Impact 125 °C
257 °F
UL 746B
Oxygen Index 45 %
45 %
ISO 4589
Glow Wire Test 875 °C
1610 °F
IEC 60695-2-13
960 °C

@Thickness 1.00 mm
1760 °F

@Thickness 0.0394 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Dielectric Constant 2.79

@Frequency 1.00e+9 Hz
2.79

@Frequency 1.00e+9 Hz
ASTM ES 7-83
Dissipation Factor 0.0058

@Frequency 1.10e+9 Hz
0.0058

@Frequency 1.10e+9 Hz
ASTM ES 7-83
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Pass
IEC 60695-10-2
FAA Flammability, FAR 25.853 A/B PASSES
FAR 25.853
NBS Smoke Density, Flaming, Dmax 70
ASTM E 662
UV-light, water exposure/immersion F1
UL 746C
Vertical Burn a (60s) passes at 5sec
FAR 25.853
Vertical Burn b (12s) passes at 5sec
FAR 25.853